General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.7 g/cm³ Show Material materials with Density of 7.7 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 220 GPa Show Material materials with Elastic modulus of 220 GPa | |
100.0 °C | 215 GPa Show Material materials with Elastic modulus of 215 GPa | ||
200.0 °C | 210 GPa Show Material materials with Elastic modulus of 210 GPa | ||
300.0 °C | 205 GPa Show Material materials with Elastic modulus of 205 GPa | ||
400.0 °C | 195 GPa Show Material materials with Elastic modulus of 195 GPa | ||
Elongation | 20.0 °C | 8 - 20 % Show Material materials with Elongation of 8 - 20 % | |
Elongation A80 | 20.0 °C | 18 - 20 % Show Material materials with Elongation A80 of 18 - 20 % | |
Elongation A80, transverse | 20.0 °C | 18 - 20 % Show Material materials with Elongation A80, transverse of 18 - 20 % | |
Elongation, transverse | 20.0 °C | 18 - 20 % Show Material materials with Elongation, transverse of 18 - 20 % | |
Hardness, Brinell | 20.0 °C | 200 [-] Show Material materials with Hardness, Brinell of 200 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Ferritic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Ferritic Stainless Steel |
Tensile strength | 20.0 °C | 400 - 950 MPa Show Material materials with Tensile strength of 400 - 950 MPa | |
Tensile strength, transverse | 20.0 °C | 430 - 630 MPa Show Material materials with Tensile strength, transverse of 430 - 630 MPa | |
Yield strength Rp0.2 | 20.0 °C | 200 - 320 MPa Show Material materials with Yield strength Rp0.2 of 200 - 320 MPa | |
100.0 °C | 220 MPa Show Material materials with Yield strength Rp0.2 of 220 MPa | ||
150.0 °C | 215 MPa Show Material materials with Yield strength Rp0.2 of 215 MPa | ||
200.0 °C | 210 MPa Show Material materials with Yield strength Rp0.2 of 210 MPa | ||
250.0 °C | 205 MPa Show Material materials with Yield strength Rp0.2 of 205 MPa | ||
300.0 °C | 200 MPa Show Material materials with Yield strength Rp0.2 of 200 MPa | ||
350.0 °C | 195 MPa Show Material materials with Yield strength Rp0.2 of 195 MPa | ||
400.0 °C | 190 - 196 MPa Show Material materials with Yield strength Rp0.2 of 190 - 196 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 260 - 280 MPa Show Material materials with Yield strength Rp0.2, transverse of 260 - 280 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 1/K | |
200.0 °C | 1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 1/K | ||
300.0 °C | 1.05E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.05E-5 1/K | ||
400.0 °C | 1.05E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.05E-5 1/K | ||
500.0 °C | 1.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-5 1/K | ||
Melting point | 1425 - 1530 °C Show Material materials with Melting point of 1425 - 1530 °C | Typical for Ferritic Stainless Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 25 W/(m·K) Show Material materials with Thermal conductivity of 25 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 6E-7 Ω·m Show Material materials with Electrical resistivity of 6E-7 Ω·m |
Chemical properties
Property | Value |
---|---|
Carbon | 0.08 % Show Material materials with Carbon of 0.08 % |
Chromium | 16 - 18 % Show Material materials with Chromium of 16 - 18 % |
Manganese | 1 % Show Material materials with Manganese of 1 % |
Phosphorus | 0.04 % Show Material materials with Phosphorus of 0.04 % |
Silicon | 1 % Show Material materials with Silicon of 1 % |
Sulfur | 0.015 % Show Material materials with Sulfur of 0.015 % |