General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 200 - 212 GPa Show Material materials with Elastic modulus of 200 - 212 GPa | |
100.0 °C | 194 - 206 GPa Show Material materials with Elastic modulus of 194 - 206 GPa | ||
200.0 °C | 186 GPa Show Material materials with Elastic modulus of 186 GPa | ||
300.0 °C | 180 GPa Show Material materials with Elastic modulus of 180 GPa | ||
Elongation | 20.0 °C | 12 - 25 % Show Material materials with Elongation of 12 - 25 % | |
Elongation A80, transverse | 20.0 °C | 20 - 25 % Show Material materials with Elongation A80, transverse of 20 - 25 % | |
Elongation, transverse | 20.0 °C | 20 - 25 % Show Material materials with Elongation, transverse of 20 - 25 % | |
Hardness, Brinell | 20.0 °C | 270 [-] Show Material materials with Hardness, Brinell of 270 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Duplex Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Duplex Stainless Steel |
Tensile strength | 20.0 °C | 650 - 1150 MPa Show Material materials with Tensile strength of 650 - 1150 MPa | |
Tensile strength, transverse | 20.0 °C | 640 - 950 MPa Show Material materials with Tensile strength, transverse of 640 - 950 MPa | |
Yield strength Rp0.2 | 20.0 °C | 450 - 650 MPa Show Material materials with Yield strength Rp0.2 of 450 - 650 MPa | |
100.0 °C | 360 MPa Show Material materials with Yield strength Rp0.2 of 360 MPa | ||
150.0 °C | 335 MPa Show Material materials with Yield strength Rp0.2 of 335 MPa | ||
200.0 °C | 315 MPa Show Material materials with Yield strength Rp0.2 of 315 MPa | ||
250.0 °C | 300 MPa Show Material materials with Yield strength Rp0.2 of 300 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 460 - 500 MPa Show Material materials with Yield strength Rp0.2, transverse of 460 - 500 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.3E-5 - 1.33E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 - 1.33E-5 1/K | |
200.0 °C | 1.35E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.35E-5 1/K | ||
300.0 °C | 1.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.4E-5 1/K | ||
Max service temperature | 300 °C Show Material materials with Max service temperature of 300 °C | Typical for Duplex Stainless Steel | |
Melting point | 1375 - 1450 °C Show Material materials with Melting point of 1375 - 1450 °C | Typical for Duplex Stainless Steel | |
Specific heat capacity | 20.0 °C | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 13.4 - 15 W/(m·K) Show Material materials with Thermal conductivity of 13.4 - 15 W/(m·K) | |
100.0 °C | 14.9 W/(m·K) Show Material materials with Thermal conductivity of 14.9 W/(m·K) | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 7.85E-7 - 8E-7 Ω·m Show Material materials with Electrical resistivity of 7.85E-7 - 8E-7 Ω·m |
100.0 °C | 8.44E-7 Ω·m Show Material materials with Electrical resistivity of 8.44E-7 Ω·m | |
Chemical properties
Property | Value |
---|---|
Carbon | 0.03 % Show Material materials with Carbon of 0.03 % |
Chromium | 21 - 23 % Show Material materials with Chromium of 21 - 23 % |
Manganese | 2 % Show Material materials with Manganese of 2 % |
Molybdenum | 2.5 - 3.5 % Show Material materials with Molybdenum of 2.5 - 3.5 % |
Nickel | 4.5 - 6.5 % Show Material materials with Nickel of 4.5 - 6.5 % |
Nitrogen | 0.1 - 0.22 % Show Material materials with Nitrogen of 0.1 - 0.22 % |
Phosphorus | 0.04 % Show Material materials with Phosphorus of 0.04 % |
Silicon | 1 % Show Material materials with Silicon of 1 % |
Sulfur | 0.015 % Show Material materials with Sulfur of 0.015 % |