General
Property | Value | Comment |
---|---|---|
Carbon equivalent (CEV) | 0.47 [-] Show Material materials with Carbon equivalent (CEV) of 0.47 [-] | max. |
Density | 7.85 g/cm³ Show Material materials with Density of 7.85 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | -40 °C | 60 J Show Material materials with Charpy impact energy, V-notch of 60 J | Charpy in transverse direction, for t > 40 mm also tested on specimens from half plate thickness |
Elongation | 15 % Show Material materials with Elongation of 15 % | min. | |
Tensile strength | 540 - 740 MPa Show Material materials with Tensile strength of 540 - 740 MPa | range depending on the thickness | |
Yield strength | 440 - 500 MPa Show Material materials with Yield strength of 440 - 500 MPa | ReH, min. values depending on the thickness, If not apparent, the yield strength Rp0.2 is measured |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.015 - 0.055 % Show Material materials with Aluminium of 0.015 - 0.055 % | |
Carbon | 0.14 % Show Material materials with Carbon of 0.14 % | max. |
Chromium | 0.3 % Show Material materials with Chromium of 0.3 % | max. |
Copper | 0.35 % Show Material materials with Copper of 0.35 % | max. |
Manganese | 2 % Show Material materials with Manganese of 2 % | max. |
Molybdenum | 0.25 % Show Material materials with Molybdenum of 0.25 % | max. |
Nickel | 1 % Show Material materials with Nickel of 1 % | max. |
Niobium | 0.05 % Show Material materials with Niobium of 0.05 % | max. |
Nitrogen | 0.01 % Show Material materials with Nitrogen of 0.01 % | max. |
Phosphorus | 0.02 % Show Material materials with Phosphorus of 0.02 % | max. |
Silicon | 0.55 % Show Material materials with Silicon of 0.55 % | max. |
Sulfur | 0.01 % Show Material materials with Sulfur of 0.01 % | max. |
Titanium | 0.025 % Show Material materials with Titanium of 0.025 % | max. |
Vanadium | 0.08 % Show Material materials with Vanadium of 0.08 % | max. |
Technological properties
Property | ||
---|---|---|
Other | The level of residual elements of arsenic, antimony, tin, lead, bismuth, calcium and boron should not exceed 0.03% As, 0.010% Sb, 0.020% Sn, 0.010% Pb, 0.010% Bi, 0.005% Ca and 0.0008% B | |
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |