DIN 1681 Grade GS-60 heat treated

Want to keep this datasheet? Save it now in your required format

Description

GS-52 for castings without special stress with good wearing properties, like coatings, bearing rollers, beater heads, hammers. For castings with static or dynamic stress for cog wheels, impellers, sprocket wheels, cranks, baffle plates. Suitable for surface hardening. Application between -10 and +300 °C.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value
Density	20.0 °C	7.85 g/cm³ Show Material materials with Density of 7.85 g/cm³

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	20.0 °C	196 GPa Show Material materials with Elastic modulus of 196 GPa
Elongation	20.0 °C	15 % Show Material materials with Elongation of 15 %
Poisson's ratio	23.0 °C	0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-]	Typical for Low Carbon Steel
Reduction of area	20.0 °C	21 % Show Material materials with Reduction of area of 21 %
Shear modulus	23.0 °C	82 GPa Show Material materials with Shear modulus of 82 GPa	Typical for Low Carbon Steel
Tensile strength	20.0 °C	600 MPa Show Material materials with Tensile strength of 600 MPa
Yield strength	20.0 °C	300 MPa Show Material materials with Yield strength of 300 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.32E-5 - 1.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K	Typical for Low Carbon Steel
Max service temperature		500 °C Show Material materials with Max service temperature of 500 °C	Typical for Carbon Steel
Max service temperature, long		-10 - 300 °C Show Material materials with Max service temperature, long of -10 - 300 °C
Melting point		1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C	Typical for Low Carbon Steel
Specific heat capacity	20.0 °C	460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K)
Thermal conductivity	20.0 °C	50 W/(m·K) Show Material materials with Thermal conductivity of 50 W/(m·K)

Electrical

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	1.43E-7 - 1.74E-7 Ω·m Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m	Typical for Carbon Steel

Magnetic

Property	Value	Comment
Curie temperature	770 °C Show Material materials with Curie temperature of 770 °C	Typical for Low Carbon Steel