General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.85 g/cm³ Show Material materials with Density of 7.85 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 211 GPa Show Material materials with Elastic modulus of 211 GPa | |
100.0 °C | 204 GPa Show Material materials with Elastic modulus of 204 GPa | ||
200.0 °C | 196 GPa Show Material materials with Elastic modulus of 196 GPa | ||
300.0 °C | 186 GPa Show Material materials with Elastic modulus of 186 GPa | ||
Elongation | 20.0 °C | 12 - 14 % Show Material materials with Elongation of 12 - 14 % | |
Poisson's ratio | 20.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Medium Carbon Steel |
Tensile strength | 20.0 °C | 500 - 670 MPa Show Material materials with Tensile strength of 500 - 670 MPa | |
Yield strength Rp0.2 | 20.0 °C | 360 - 400 MPa Show Material materials with Yield strength Rp0.2 of 360 - 400 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-5 1/K | |
200.0 °C | 1.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-5 1/K | ||
300.0 °C | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K | ||
Max service temperature, long | 0 - 300 °C Show Material materials with Max service temperature, long of 0 - 300 °C | ||
Melting point | 1380 - 1514 °C Show Material materials with Melting point of 1380 - 1514 °C | Typical for Medium Carbon Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.27 - 0.34 % Show Material materials with Carbon of 0.27 - 0.34 % |
Manganese | 1.2 - 1.5 % Show Material materials with Manganese of 1.2 - 1.5 % |
Phosphorus | 0.02 % Show Material materials with Phosphorus of 0.02 % |
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % |
Sulfur | 0.015 % Show Material materials with Sulfur of 0.015 % |