EN 10213-4 Grade GX5CrNiMo19-11-2 solution heat-treated and quenched

Want to keep this datasheet? Save it now in your required format

Description

Material GX5CrNiMo19-11-2 is equivalent to trademark G-X6 CrNiMo 18 10 acc. to DIN 17445-84. This material is used for fittings, pumps, agitators, filters and tanks in chemical industry, textile, viscose and cellulose industry. It is weldable without preheating. It is unsuitable for corrosion application where smaller welds would basically require a heat treatment.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.9 g/cm³

Show Material materials with Density of 7.9 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

195 GPa

Show Material materials with Elastic modulus of 195 GPa

Typical for Austenitic Stainless Steel

Elongation

20.0 °C

30 %

Show Material materials with Elongation of 30 %

Poisson's ratio

23.0 °C

0.3 [-]

Show Material materials with Poisson's ratio of 0.3 [-]

Typical for Austenitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Show Material materials with Shear modulus of 77 GPa

Typical for Austenitic Stainless Steel

Tensile strength

20.0 °C

440 - 640 MPa

Show Material materials with Tensile strength of 440 - 640 MPa

Yield strength Rp1.0

20.0 °C

210 MPa

Show Material materials with Yield strength Rp1.0 of 210 MPa

100.0 °C

170 MPa

Show Material materials with Yield strength Rp1.0 of 170 MPa

200.0 °C

135 MPa

Show Material materials with Yield strength Rp1.0 of 135 MPa

300.0 °C

115 MPa

Show Material materials with Yield strength Rp1.0 of 115 MPa

400.0 °C

105 MPa

Show Material materials with Yield strength Rp1.0 of 105 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.58E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.58E-5 1/K

300.0 °C

1.7E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.7E-5 1/K

500.0 °C

1.77E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.77E-5 1/K

Unlock all property charts

Max service temperature, long

-196 - 550 °C

Show Material materials with Max service temperature, long of -196 - 550 °C

Melting point

1230 - 1480 °C

Show Material materials with Melting point of 1230 - 1480 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

20.0 °C

530 J/(kg·K)

Show Material materials with Specific heat capacity of 530 J/(kg·K)

Thermal conductivity

50.0 °C

14.5 W/(m·K)

Show Material materials with Thermal conductivity of 14.5 W/(m·K)

100.0 °C

15.8 W/(m·K)

Show Material materials with Thermal conductivity of 15.8 W/(m·K)

Unlock all property charts

Electrical

PropertyTemperatureValueComment

Electrical resistivity

23.0 °C

8.5E-7 Ω·m

Show Material materials with Electrical resistivity of 8.5E-7 Ω·m

Typical for Austenitic Stainless Steel

Chemical properties

PropertyValue

Carbon

0.07 %

Show Material materials with Carbon of 0.07 %

Chromium

18 - 20 %

Show Material materials with Chromium of 18 - 20 %

Manganese

1.5 %

Show Material materials with Manganese of 1.5 %

Molybdenum

2 - 2.5 %

Show Material materials with Molybdenum of 2 - 2.5 %

Nickel

9 - 12 %

Show Material materials with Nickel of 9 - 12 %

Phosphorus

0.04 %

Show Material materials with Phosphorus of 0.04 %

Silicon

1.5 %

Show Material materials with Silicon of 1.5 %

Sulfur

0.03 %

Show Material materials with Sulfur of 0.03 %