SEW 395 Grade G-X2CrNiMoN18-14 solution heat-treated and quenched

Want to keep this datasheet? Save it now in your required format

Description

The fully austenitic material G-X 2 CrNiMoN 18 14, with the material number 1.3952 according to SEW 395-87 (invalidly replaced by GX2CrNiMoN18-14, material number 1.3960 according to SEW 395-98), possesses a defined low value of the relative magnetic permeability of 1.01 maximum (for castings with a wall thickness of up to 50 mm). It is applied for construction components which an interference or shielding of a magnetic field must not occur at. (SEW: steel-iron material specification)

Related Standards

SEW 395

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value
Density	20.0 °C	7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	195 GPa Show Material materials with Elastic modulus of 195 GPa	Typical for Austenitic Stainless Steel
Elongation	20.0 °C	30 % Show Material materials with Elongation of 30 %
Poisson's ratio	23.0 °C	0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-]	Typical for Austenitic Stainless Steel
Shear modulus	23.0 °C	77 GPa Show Material materials with Shear modulus of 77 GPa	Typical for Austenitic Stainless Steel
Tensile strength	20.0 °C	490 - 690 MPa Show Material materials with Tensile strength of 490 - 690 MPa
Yield strength Rp0.2	20.0 °C	240 MPa Show Material materials with Yield strength Rp0.2 of 240 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	100.0 °C	1.65E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.65E-5 1/K
	200.0 °C	1.75E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.75E-5 1/K
	300.0 °C	1.75E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.75E-5 1/K

Melting point		1230 - 1480 °C Show Material materials with Melting point of 1230 - 1480 °C	Typical for Austenitic Stainless Steel
Specific heat capacity	23.0 °C	440 J/(kg·K) Show Material materials with Specific heat capacity of 440 J/(kg·K)	Typical for Austenitic Stainless Steel
Thermal conductivity	20.0 °C	15 W/(m·K) Show Material materials with Thermal conductivity of 15 W/(m·K)

Electrical

Property	Temperature	Value
Electrical resistivity	20.0 °C	7.5E-7 Ω·m Show Material materials with Electrical resistivity of 7.5E-7 Ω·m

Chemical properties

Property	Value
Carbon	0.03 % Show Material materials with Carbon of 0.03 %
Chromium	16.5 - 18.5 % Show Material materials with Chromium of 16.5 - 18.5 %
Manganese	2 % Show Material materials with Manganese of 2 %
Molybdenum	2.5 - 3 % Show Material materials with Molybdenum of 2.5 - 3 %
Nickel	13 - 15 % Show Material materials with Nickel of 13 - 15 %
Nitrogen	0.15 - 0.25 % Show Material materials with Nitrogen of 0.15 - 0.25 %
Phosphorus	0.04 % Show Material materials with Phosphorus of 0.04 %
Silicon	1 % Show Material materials with Silicon of 1 %
Sulfur	0.02 % Show Material materials with Sulfur of 0.02 %