General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.85 g/cm³ Show Material materials with Density of 7.85 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 220 GPa Show Material materials with Elastic modulus of 220 GPa | Typical for Martensitic Stainless Steel |
Elongation, transverse | 20.0 °C | 12 - 15 % Show Material materials with Elongation, transverse of 12 - 15 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel |
Reduction of area, transverse | 20.0 °C | 35 - 40 % Show Material materials with Reduction of area, transverse of 35 - 40 % | |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength, transverse | 20.0 °C | 700 - 1000 MPa Show Material materials with Tensile strength, transverse of 700 - 1000 MPa | |
Yield strength Rp0.2 | 100.0 °C | 555 - 755 MPa Show Material materials with Yield strength Rp0.2 of 555 - 755 MPa | |
200.0 °C | 525 - 725 MPa Show Material materials with Yield strength Rp0.2 of 525 - 725 MPa | ||
250.0 °C | 515 - 710 MPa Show Material materials with Yield strength Rp0.2 of 515 - 710 MPa | ||
300.0 °C | 505 - 695 MPa Show Material materials with Yield strength Rp0.2 of 505 - 695 MPa | ||
350.0 °C | 495 - 675 MPa Show Material materials with Yield strength Rp0.2 of 495 - 675 MPa | ||
400.0 °C | 475 - 650 MPa Show Material materials with Yield strength Rp0.2 of 475 - 650 MPa | ||
450.0 °C | 445 - 615 MPa Show Material materials with Yield strength Rp0.2 of 445 - 615 MPa | ||
500.0 °C | 405 - 565 MPa Show Material materials with Yield strength Rp0.2 of 405 - 565 MPa | ||
550.0 °C | 345 - 505 MPa Show Material materials with Yield strength Rp0.2 of 345 - 505 MPa | ||
600.0 °C | 270 - 425 MPa Show Material materials with Yield strength Rp0.2 of 270 - 425 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 600 - 830 MPa Show Material materials with Yield strength Rp0.2, transverse of 600 - 830 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-5 - 1.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K | Typical for Martensitic Stainless Steel |
Max service temperature, long | 0 - 600 °C Show Material materials with Max service temperature, long of 0 - 600 °C | ||
Melting point | 1370 - 1530 °C Show Material materials with Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 23.0 °C | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | Typical for Martensitic Stainless Steel |
Thermal conductivity | 23.0 °C | 14 - 31 W/(m·K) Show Material materials with Thermal conductivity of 14 - 31 W/(m·K) | Typical for Martensitic Stainless Steel |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 6E-7 Ω·m Show Material materials with Electrical resistivity of 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.012 % Show Material materials with Aluminium of 0.012 % |
Carbon | 0.1 - 0.14 % Show Material materials with Carbon of 0.1 - 0.14 % |
Chromium | 10 - 11 % Show Material materials with Chromium of 10 - 11 % |
Manganese | 0.4 - 0.6 % Show Material materials with Manganese of 0.4 - 0.6 % |
Molybdenum | 1 - 1.2 % Show Material materials with Molybdenum of 1 - 1.2 % |
Nickel | 0.6 - 0.8 % Show Material materials with Nickel of 0.6 - 0.8 % |
Niobium | 0.04 - 0.06 % Show Material materials with Niobium of 0.04 - 0.06 % |
Nitrogen | 0.04 - 0.06 % Show Material materials with Nitrogen of 0.04 - 0.06 % |
Phosphorus | 0.02 % Show Material materials with Phosphorus of 0.02 % |
Silicon | 0.1 % Show Material materials with Silicon of 0.1 % |
Sulfur | 7E-3 % Show Material materials with Sulfur of 7E-3 % |
Tungsten | 0.95 - 1.1 % Show Material materials with Tungsten of 0.95 - 1.1 % |
Vanadium | 0.15 - 0.25 % Show Material materials with Vanadium of 0.15 - 0.25 % |