EN 10025 Grade S235JRG2C as-rolled condition (+AR)

Want to keep this datasheet? Save it now in your required format

Description

S235JRG2C is used for folding, section cold forming and cold drawing grades. The steel is applicable for welding constructions up to -20 °C subject to the load. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades. As a bright-steel product it is used in the form of bars, bright, straight in various conditions (see DIN EN 10277 : 1999-10).

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³	Typical for Low Carbon Steel

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa	Typical for Low Carbon Steel
Elongation	20.0 °C	26 % Show Material materials with Elongation of 26 %
Elongation A80	20.0 °C	17 - 21 % Show Material materials with Elongation A80 of 17 - 21 %
Elongation A80, transverse	20.0 °C	15 - 19 % Show Material materials with Elongation A80, transverse of 15 - 19 %
Elongation, transverse	20.0 °C	24 % Show Material materials with Elongation, transverse of 24 %
Poisson's ratio	23.0 °C	0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-]	Typical for Low Carbon Steel
Shear modulus	23.0 °C	82 GPa Show Material materials with Shear modulus of 82 GPa	Typical for Low Carbon Steel
Tensile strength	20.0 °C	340 - 510 MPa Show Material materials with Tensile strength of 340 - 510 MPa
Tensile strength, transverse	20.0 °C	340 - 510 MPa Show Material materials with Tensile strength, transverse of 340 - 510 MPa
Yield strength	20.0 °C	225 - 235 MPa Show Material materials with Yield strength of 225 - 235 MPa
Yield strength, transverse	20.0 °C	225 - 235 MPa Show Material materials with Yield strength, transverse of 225 - 235 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.32E-5 - 1.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K	Typical for Low Carbon Steel
Max service temperature		500 °C Show Material materials with Max service temperature of 500 °C	Typical for Carbon Steel
Max service temperature, long		-20 - 0 °C Show Material materials with Max service temperature, long of -20 - 0 °C
Melting point		1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C	Typical for Low Carbon Steel
Specific heat capacity	23.0 °C	465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K)	Typical for Low Carbon Steel
Thermal conductivity	23.0 °C	25 - 93 W/(m·K) Show Material materials with Thermal conductivity of 25 - 93 W/(m·K)	Typical for Low Carbon Steel

Electrical

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	1.43E-7 - 1.74E-7 Ω·m Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m	Typical for Carbon Steel

Magnetic

Property	Value	Comment
Curie temperature	770 °C Show Material materials with Curie temperature of 770 °C	Typical for Low Carbon Steel

Chemical properties

Property	Value
Carbon	0.17 % Show Material materials with Carbon of 0.17 %
Manganese	1.4 % Show Material materials with Manganese of 1.4 %
Nitrogen	9E-3 % Show Material materials with Nitrogen of 9E-3 %
Phosphorus	0.05 % Show Material materials with Phosphorus of 0.05 %
Sulfur	0.045 % Show Material materials with Sulfur of 0.045 %

Looking for suppliers of this material? Click to see 1 supplier of EN 10025 Grade S235JRG2C as-rolled condition (+AR) on Matmatch

Do you have a technical question or need more information about this material?

Post it as a comment below and receive answers from engineers and other community members.