General
Property | Value | Comment |
---|---|---|
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel | ||||
Elongation | 19.7 % Show Material materials with Elongation of 19.7 % | Predicted Value, A200 | ||||
20.3 % Show Material materials with Elongation of 20.3 % | Predicted Value, Transverse | |||||
21.5 % Show Material materials with Elongation of 21.5 % | Predicted Value, A5 | |||||
24.9 % Show Material materials with Elongation of 24.9 % | Predicted Value, A80 Transverse | |||||
27.8 % Show Material materials with Elongation of 27.8 % | Predicted Value, A50 | |||||
31.8 % Show Material materials with Elongation of 31.8 % | Predicted Value | |||||
20 °C | 28 % Show Material materials with Elongation of 28 % | skin passed | EN 10130 | Sheet, Flat, Bar, Strip | A80 | |
Hardness, Brinell | 263 [-] Show Material materials with Hardness, Brinell of 263 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel | ||||
Reduction of area | 43.3 % Show Material materials with Reduction of area of 43.3 % | Predicted Value, Transverse | ||||
44.8 % Show Material materials with Reduction of area of 44.8 % | Predicted Value | |||||
Shear modulus | 82 GPa Show Material materials with Shear modulus of 82 GPa | Typical for Low Carbon Steel | ||||
Shear strength | 526.2 MPa Show Material materials with Shear strength of 526.2 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 270 - 410 MPa Show Material materials with Tensile strength of 270 - 410 MPa | skin passed | EN 10130 | Sheet, Flat, Bar, Strip | |
Yield strength | 257.3 MPa Show Material materials with Yield strength of 257.3 MPa | Predicted Value, RP1 | ||||
258.4 MPa Show Material materials with Yield strength of 258.4 MPa | Predicted Value, RP05 | |||||
284.1 MPa Show Material materials with Yield strength of 284.1 MPa | Predicted Value, Transverse | |||||
309.1 MPa Show Material materials with Yield strength of 309.1 MPa | Predicted Value, RP02 | |||||
315 MPa Show Material materials with Yield strength of 315 MPa | Predicted Value, RP1 Transverse | |||||
455.1 MPa Show Material materials with Yield strength of 455.1 MPa | Predicted Value, RP02 Transverse | |||||
489.2 MPa Show Material materials with Yield strength of 489.2 MPa | Predicted Value, RP002 | |||||
20 °C | 140 - 280 MPa Show Material materials with Yield strength of 140 - 280 MPa | skin passed | EN 10130 | Sheet, Flat, Bar, Strip |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.32e-05 - 1.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
Max service temperature | 327.5 °C Show Material materials with Max service temperature of 327.5 °C | Predicted Value, Long |
500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Specific heat capacity | 465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 25 - 93 W/(m·K) Show Material materials with Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 8 S/m Show Material materials with Electrical conductivity of 8 S/m | Predicted Value |
Electrical resistivity | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Carbon | 0.12 % Show Material materials with Carbon of 0.12 % | skin passed | EN 10130 | Sheet, Flat, Bar, Strip |
Manganese | 0.6 % Show Material materials with Manganese of 0.6 % | skin passed | EN 10130 | Sheet, Flat, Bar, Strip |
Phosphorus | 0.045 % Show Material materials with Phosphorus of 0.045 % | skin passed | EN 10130 | Sheet, Flat, Bar, Strip |
Sulfur | 0.045 % Show Material materials with Sulfur of 0.045 % | skin passed | EN 10130 | Sheet, Flat, Bar, Strip |