General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.7 g/cm³ Show Material materials with Density of 7.7 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 210 GPa Show Material materials with Elastic modulus of 210 GPa | |
Elongation | 20.0 °C | 14 % Show Material materials with Elongation of 14 % | |
Hardness, Brinell | 20.0 °C | 266 - 325 [-] Show Material materials with Hardness, Brinell of 266 - 325 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel |
Reduction of area | 20.0 °C | 40 % Show Material materials with Reduction of area of 40 % | |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 20.0 °C | 900 - 1100 MPa Show Material materials with Tensile strength of 900 - 1100 MPa | |
500.0 °C | 550 MPa Show Material materials with Tensile strength of 550 MPa | ||
550.0 °C | 420 MPa Show Material materials with Tensile strength of 420 MPa | ||
600.0 °C | 300 MPa Show Material materials with Tensile strength of 300 MPa | ||
650.0 °C | 220 MPa Show Material materials with Tensile strength of 220 MPa | ||
700.0 °C | 130 MPa Show Material materials with Tensile strength of 130 MPa | ||
Yield strength Rp0.2 | 20.0 °C | 700 MPa Show Material materials with Yield strength Rp0.2 of 700 MPa | |
500.0 °C | 450 MPa Show Material materials with Yield strength Rp0.2 of 450 MPa | ||
550.0 °C | 350 MPa Show Material materials with Yield strength Rp0.2 of 350 MPa | ||
600.0 °C | 200 MPa Show Material materials with Yield strength Rp0.2 of 200 MPa | ||
650.0 °C | 180 MPa Show Material materials with Yield strength Rp0.2 of 180 MPa | ||
700.0 °C | 100 MPa Show Material materials with Yield strength Rp0.2 of 100 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.09E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.09E-5 1/K | |
300.0 °C | 1.12E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.12E-5 1/K | ||
500.0 °C | 1.15E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.15E-5 1/K | ||
700.0 °C | 1.18E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.18E-5 1/K | ||
Melting point | 1370 - 1530 °C Show Material materials with Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 21 W/(m·K) Show Material materials with Thermal conductivity of 21 W/(m·K) |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 6E-7 Ω·m Show Material materials with Electrical resistivity of 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.35 - 0.45 % Show Material materials with Carbon of 0.35 - 0.45 % |
Chromium | 9.5 - 11.5 % Show Material materials with Chromium of 9.5 - 11.5 % |
Manganese | 0.8 % Show Material materials with Manganese of 0.8 % |
Molybdenum | 0.8 - 1.3 % Show Material materials with Molybdenum of 0.8 - 1.3 % |
Nickel | 0.5 % Show Material materials with Nickel of 0.5 % |
Phosphorus | 0.04 % Show Material materials with Phosphorus of 0.04 % |
Silicon | 2 - 3 % Show Material materials with Silicon of 2 - 3 % |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % |