General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 205 GPa Show Material materials with Elastic modulus of 205 GPa | |
Elongation | 20.0 °C | 8 % Show Material materials with Elongation of 8 % | |
Hardness, Rockwell C | 20.0 °C | 28 [-] Show Material materials with Hardness, Rockwell C of 28 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
Reduction of area | 20.0 °C | 10 % Show Material materials with Reduction of area of 10 % | |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
Tensile strength | 20.0 °C | 900 - 1150 MPa Show Material materials with Tensile strength of 900 - 1150 MPa | |
500.0 °C | 640 MPa Show Material materials with Tensile strength of 640 MPa | ||
550.0 °C | 590 MPa Show Material materials with Tensile strength of 590 MPa | ||
600.0 °C | 540 MPa Show Material materials with Tensile strength of 540 MPa | ||
650.0 °C | 490 MPa Show Material materials with Tensile strength of 490 MPa | ||
700.0 °C | 440 MPa Show Material materials with Tensile strength of 440 MPa | ||
750.0 °C | 360 MPa Show Material materials with Tensile strength of 360 MPa | ||
800.0 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | ||
Yield strength Rp0.2 | 20.0 °C | 550 MPa Show Material materials with Yield strength Rp0.2 of 550 MPa | |
500.0 °C | 300 MPa Show Material materials with Yield strength Rp0.2 of 300 MPa | ||
550.0 °C | 280 MPa Show Material materials with Yield strength Rp0.2 of 280 MPa | ||
600.0 °C | 250 MPa Show Material materials with Yield strength Rp0.2 of 250 MPa | ||
650.0 °C | 230 MPa Show Material materials with Yield strength Rp0.2 of 230 MPa | ||
700.0 °C | 220 MPa Show Material materials with Yield strength Rp0.2 of 220 MPa | ||
750.0 °C | 200 MPa Show Material materials with Yield strength Rp0.2 of 200 MPa | ||
800.0 °C | 170 MPa Show Material materials with Yield strength Rp0.2 of 170 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.55E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.55E-5 1/K | |
300.0 °C | 1.75E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.75E-5 1/K | ||
500.0 °C | 1.85E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.85E-5 1/K | ||
700.0 °C | 1.88E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.88E-5 1/K | ||
Melting point | 1230 - 1480 °C Show Material materials with Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 14.5 W/(m·K) Show Material materials with Thermal conductivity of 14.5 W/(m·K) |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 8.5E-7 Ω·m Show Material materials with Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.5 - 0.6 % Show Material materials with Carbon of 0.5 - 0.6 % |
Chromium | 19.5 - 21.5 % Show Material materials with Chromium of 19.5 - 21.5 % |
Manganese | 7 - 10 % Show Material materials with Manganese of 7 - 10 % |
Nickel | 1.5 - 2.75 % Show Material materials with Nickel of 1.5 - 2.75 % |
Nitrogen | 0.2 - 0.4 % Show Material materials with Nitrogen of 0.2 - 0.4 % |
Phosphorus | 0.05 % Show Material materials with Phosphorus of 0.05 % |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % |