General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 205 GPa Show Material materials with Elastic modulus of 205 GPa | |
Elongation | 20.0 °C | 20 % Show Material materials with Elongation of 20 % | |
Hardness, Rockwell C | 20.0 °C | 25 [-] Show Material materials with Hardness, Rockwell C of 25 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
Reduction of area | 20.0 °C | 30 % Show Material materials with Reduction of area of 30 % | |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
Tensile strength | 20.0 °C | 850 - 1100 MPa Show Material materials with Tensile strength of 850 - 1100 MPa | |
500.0 °C | 600 MPa Show Material materials with Tensile strength of 600 MPa | ||
550.0 °C | 570 MPa Show Material materials with Tensile strength of 570 MPa | ||
600.0 °C | 530 MPa Show Material materials with Tensile strength of 530 MPa | ||
650.0 °C | 470 MPa Show Material materials with Tensile strength of 470 MPa | ||
700.0 °C | 400 MPa Show Material materials with Tensile strength of 400 MPa | ||
750.0 °C | 340 MPa Show Material materials with Tensile strength of 340 MPa | ||
800.0 °C | 280 MPa Show Material materials with Tensile strength of 280 MPa | ||
Yield strength Rp0.2 | 20.0 °C | 550 MPa Show Material materials with Yield strength Rp0.2 of 550 MPa | |
500.0 °C | 270 MPa Show Material materials with Yield strength Rp0.2 of 270 MPa | ||
550.0 °C | 250 MPa Show Material materials with Yield strength Rp0.2 of 250 MPa | ||
600.0 °C | 220 MPa Show Material materials with Yield strength Rp0.2 of 220 MPa | ||
650.0 °C | 210 MPa Show Material materials with Yield strength Rp0.2 of 210 MPa | ||
700.0 °C | 190 MPa Show Material materials with Yield strength Rp0.2 of 190 MPa | ||
750.0 °C | 180 MPa Show Material materials with Yield strength Rp0.2 of 180 MPa | ||
800.0 °C | 170 MPa Show Material materials with Yield strength Rp0.2 of 170 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.65E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.65E-5 1/K | |
300.0 °C | 1.71E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.71E-5 1/K | ||
500.0 °C | 1.73E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.73E-5 1/K | ||
700.0 °C | 1.74E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.74E-5 1/K | ||
Melting point | 1230 - 1480 °C Show Material materials with Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 14.5 W/(m·K) Show Material materials with Thermal conductivity of 14.5 W/(m·K) |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 8.5E-7 Ω·m Show Material materials with Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.28 - 0.38 % Show Material materials with Carbon of 0.28 - 0.38 % |
Chromium | 22 - 24 % Show Material materials with Chromium of 22 - 24 % |
Manganese | 1.5 - 3.5 % Show Material materials with Manganese of 1.5 - 3.5 % |
Molybdenum | 0.5 % Show Material materials with Molybdenum of 0.5 % |
Nickel | 7 - 9 % Show Material materials with Nickel of 7 - 9 % |
Nitrogen | 0.25 - 0.35 % Show Material materials with Nitrogen of 0.25 - 0.35 % |
Phosphorus | 0.05 % Show Material materials with Phosphorus of 0.05 % |
Silicon | 0.5 - 1 % Show Material materials with Silicon of 0.5 - 1 % |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % |
Tungsten | 0.5 % Show Material materials with Tungsten of 0.5 % |