General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Molybdenum Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Molybdenum Steel |
Elongation | 20.0 °C | 19 % Show Material materials with Elongation of 19 % | |
Elongation, transverse | 20.0 °C | 17 % Show Material materials with Elongation, transverse of 17 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Molybdenum Steel |
Tensile strength | 20.0 °C | 540 - 690 MPa Show Material materials with Tensile strength of 540 - 690 MPa | |
Tensile strength, transverse | 20.0 °C | 540 - 690 MPa Show Material materials with Tensile strength, transverse of 540 - 690 MPa | |
Yield strength Rp0.2 | 20.0 °C | 400 MPa Show Material materials with Yield strength Rp0.2 of 400 MPa | |
100.0 °C | 368 MPa Show Material materials with Yield strength Rp0.2 of 368 MPa | ||
150.0 °C | 368 MPa Show Material materials with Yield strength Rp0.2 of 368 MPa | ||
200.0 °C | 368 MPa Show Material materials with Yield strength Rp0.2 of 368 MPa | ||
250.0 °C | 368 MPa Show Material materials with Yield strength Rp0.2 of 368 MPa | ||
300.0 °C | 368 MPa Show Material materials with Yield strength Rp0.2 of 368 MPa | ||
350.0 °C | 368 MPa Show Material materials with Yield strength Rp0.2 of 368 MPa | ||
400.0 °C | 368 MPa Show Material materials with Yield strength Rp0.2 of 368 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 400 MPa Show Material materials with Yield strength Rp0.2, transverse of 400 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.29E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.29E-5 1/K | Typical for Molybdenum Steel |
Max service temperature, long | 200 - 550 °C Show Material materials with Max service temperature, long of 200 - 550 °C | ||
Melting point | 1382 - 1529 °C Show Material materials with Melting point of 1382 - 1529 °C | Typical for Molybdenum Steel | |
Specific heat capacity | 23.0 °C | 456 J/(kg·K) Show Material materials with Specific heat capacity of 456 J/(kg·K) | Typical for Molybdenum Steel |
Thermal conductivity | 23.0 °C | 37 - 48 W/(m·K) Show Material materials with Thermal conductivity of 37 - 48 W/(m·K) | Typical for Molybdenum Steel |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.06 % Show Material materials with Aluminium of 0.06 % |
Boron | 2E-3 - 6E-3 % Show Material materials with Boron of 2E-3 - 6E-3 % |
Carbon | 0.06 - 0.1 % Show Material materials with Carbon of 0.06 - 0.1 % |
Chromium | 0.2 % Show Material materials with Chromium of 0.2 % |
Copper | 0.3 % Show Material materials with Copper of 0.3 % |
Manganese | 0.6 - 0.8 % Show Material materials with Manganese of 0.6 - 0.8 % |
Molybdenum | 0.4 - 0.5 % Show Material materials with Molybdenum of 0.4 - 0.5 % |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % |
Silicon | 0.1 - 0.35 % Show Material materials with Silicon of 0.1 - 0.35 % |
Sulfur | 0.01 - 0.02 % Show Material materials with Sulfur of 0.01 - 0.02 % |
Titanium | 0.06 % Show Material materials with Titanium of 0.06 % |