General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Chromium Molybdenum Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Chromium Molybdenum Steel |
Elongation | 20.0 °C | 15 % Show Material materials with Elongation of 15 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Chromium Molybdenum Steel |
Reduction of area | 20.0 °C | 50 % Show Material materials with Reduction of area of 50 % | |
Tensile strength | 20.0 °C | 820 - 1000 MPa Show Material materials with Tensile strength of 820 - 1000 MPa | |
Yield strength Rp0.2 | 20.0 °C | 660 MPa Show Material materials with Yield strength Rp0.2 of 660 MPa | |
50.0 °C | 642 MPa Show Material materials with Yield strength Rp0.2 of 642 MPa | ||
100.0 °C | 624 MPa Show Material materials with Yield strength Rp0.2 of 624 MPa | ||
150.0 °C | 603 MPa Show Material materials with Yield strength Rp0.2 of 603 MPa | ||
200.0 °C | 595 MPa Show Material materials with Yield strength Rp0.2 of 595 MPa | ||
250.0 °C | 581 MPa Show Material materials with Yield strength Rp0.2 of 581 MPa | ||
300.0 °C | 573 MPa Show Material materials with Yield strength Rp0.2 of 573 MPa | ||
350.0 °C | 559 MPa Show Material materials with Yield strength Rp0.2 of 559 MPa | ||
400.0 °C | 537 MPa Show Material materials with Yield strength Rp0.2 of 537 MPa | ||
450.0 °C | 508 MPa Show Material materials with Yield strength Rp0.2 of 508 MPa | ||
500.0 °C | 464 MPa Show Material materials with Yield strength Rp0.2 of 464 MPa | ||
550.0 °C | 406 MPa Show Material materials with Yield strength Rp0.2 of 406 MPa | ||
600.0 °C | 334 MPa Show Material materials with Yield strength Rp0.2 of 334 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-5 - 1.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K | Typical for Chromium Molybdenum Steel |
Melting point | 1382 - 1529 °C Show Material materials with Melting point of 1382 - 1529 °C | Typical for Chromium Molybdenum Steel | |
Specific heat capacity | 23.0 °C | 448 - 502 J/(kg·K) Show Material materials with Specific heat capacity of 448 - 502 J/(kg·K) | Typical for Chromium Molybdenum Steel |
Thermal conductivity | 23.0 °C | 36 - 43 W/(m·K) Show Material materials with Thermal conductivity of 36 - 43 W/(m·K) | Typical for Chromium Molybdenum Steel |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.015 - 0.08 % Show Material materials with Aluminium of 0.015 - 0.08 % |
Arsenic | 0.02 % Show Material materials with Arsenic of 0.02 % |
Boron | 0.001 - 0.01 % Show Material materials with Boron of 0.001 - 0.01 % |
Carbon | 0.17 - 0.23 % Show Material materials with Carbon of 0.17 - 0.23 % |
Chromium | 0.9 - 1.2 % Show Material materials with Chromium of 0.9 - 1.2 % |
Copper | 0.2 % Show Material materials with Copper of 0.2 % |
Manganese | 0.35 - 0.75 % Show Material materials with Manganese of 0.35 - 0.75 % |
Molybdenum | 0.9 - 1.1 % Show Material materials with Molybdenum of 0.9 - 1.1 % |
Nickel | 0.2 % Show Material materials with Nickel of 0.2 % |
Phosphorus | 0.02 % Show Material materials with Phosphorus of 0.02 % |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % |
Sulfur | 0.015 - 0.02 % Show Material materials with Sulfur of 0.015 - 0.02 % |
Tin | 0.02 % Show Material materials with Tin of 0.02 % |
Titanium | 0.07 - 0.15 % Show Material materials with Titanium of 0.07 - 0.15 % |
Vanadium | 0.6 - 0.8 % Show Material materials with Vanadium of 0.6 - 0.8 % |