General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 20.0 °C | 24 % Show Material materials with Elongation of 24 % | |
Elongation A50 | 20.0 °C | 20 % Show Material materials with Elongation A50 of 20 % | |
Elongation A80 | 20.0 °C | 18 % Show Material materials with Elongation A80 of 18 % | |
Hardness, Vickers | 20.0 °C | 95 - 125 [-] Show Material materials with Hardness, Vickers of 95 - 125 [-] | |
Poisson's ratio | 20.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 290 - 430 MPa Show Material materials with Tensile strength of 290 - 430 MPa | |
Yield strength | 20.0 °C | 200 - 380 MPa Show Material materials with Yield strength of 200 - 380 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.32E-5 - 1.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties