General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 20.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation A5 | 20.0 °C | 17 % Show Material materials with Elongation A5 of 17 % | |
Impact strength, Charpy notched | -50.0 °C | 27 kJ/m² Show Material materials with Impact strength, Charpy notched of 27 kJ/m² | |
Poisson's ratio | 20.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 20.0 °C | 75 - 80 GPa Show Material materials with Shear modulus of 75 - 80 GPa | Typical for Carbon Steel |
Tensile strength | 20.0 °C | 510 - 720 MPa Show Material materials with Tensile strength of 510 - 720 MPa | |
Yield strength Rp0.2 | 20.0 °C | 380 - 460 MPa Show Material materials with Yield strength Rp0.2 of 380 - 460 MPa | |
impactTransVNotch | -50.0 °C | 16 kJ/m² Show Material materials with impactTransVNotch of 16 kJ/m² |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.32E-5 - 1.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 20.0 °C | 1.43E-7 - 1.74E-7 Ω·m Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Temperature | Value | Comment |
|---|---|---|---|
Curie temperature | 20.0 °C | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0 - 0.02 % Show Material materials with Aluminium of 0 - 0.02 % |
Boron | 0 - 5E-3 % Show Material materials with Boron of 0 - 5E-3 % |
Carbon | 0.2 % Show Material materials with Carbon of 0.2 % |
Chromium | 0.7 - 2 % Show Material materials with Chromium of 0.7 - 2 % |
Copper | 0.7 - 1.5 % Show Material materials with Copper of 0.7 - 1.5 % |
Iron | 90.45 - 99.3 % Show Material materials with Iron of 90.45 - 99.3 % |
Manganese | 0.7 - 1.7 % Show Material materials with Manganese of 0.7 - 1.7 % |
Molybdenum | 0.4 - 1 % Show Material materials with Molybdenum of 0.4 - 1 % |
Nickel | 1 - 2 % Show Material materials with Nickel of 1 - 2 % |
Niobium | 0 - 0.06 % Show Material materials with Niobium of 0 - 0.06 % |
Nitrogen | 0 - 0.02 % Show Material materials with Nitrogen of 0 - 0.02 % |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % |
Silicon | 0.5 - 0.55 % Show Material materials with Silicon of 0.5 - 0.55 % |
Sulfur | 0.025 - 0.03 % Show Material materials with Sulfur of 0.025 - 0.03 % |
Titanium | 0 - 0.2 % Show Material materials with Titanium of 0 - 0.2 % |
Vanadium | 0 - 0.2 % Show Material materials with Vanadium of 0 - 0.2 % |
Zirconium | 0 - 0.15 % Show Material materials with Zirconium of 0 - 0.15 % |
Technological properties
| Property | ||
|---|---|---|
| Processing history | normalized, controlled rolled | |