General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for High Carbon Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for High Carbon Steel |
Elongation A5 | 20.0 °C | 24 % Show Material materials with Elongation A5 of 24 % | |
Elongation A5, transverse | 20.0 °C | 19 % Show Material materials with Elongation A5, transverse of 19 % | |
Hardness, Brinell | 20.0 °C | 121 [-] Show Material materials with Hardness, Brinell of 121 [-] | |
Poisson's ratio | 20.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for High Carbon Steel |
Reduction of area | 20.0 °C | 45 % Show Material materials with Reduction of area of 45 % | |
Reduction of area, transverse | 20.0 °C | 35 % Show Material materials with Reduction of area, transverse of 35 % | |
Shear modulus | 20.0 °C | 75 - 80 GPa Show Material materials with Shear modulus of 75 - 80 GPa | Typical for Carbon Steel |
Tensile strength | 20.0 °C | 440 - 540 MPa Show Material materials with Tensile strength of 440 - 540 MPa | |
Yield strength | 20.0 °C | 225 MPa Show Material materials with Yield strength of 225 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.32E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 1/K | Typical for High Carbon Steel |
Max service temperature | 500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1289 - 1478 °C Show Material materials with Melting point of 1289 - 1478 °C | Typical for High Carbon Steel |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 20.0 °C | 1.43E-7 - 1.74E-7 Ω·m Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.6 % Show Material materials with Carbon of 0.6 % |
Iron | 97.63 - 99.55 % Show Material materials with Iron of 97.63 - 99.55 % |
Manganese | 0.3 - 1.2 % Show Material materials with Manganese of 0.3 - 1.2 % |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % |
Silicon | 0.15 - 0.5 % Show Material materials with Silicon of 0.15 - 0.5 % |
Sulfur | 0.035 % Show Material materials with Sulfur of 0.035 % |
Technological properties
Property | ||
---|---|---|
Processing history | annealed, normalized or normalized and tempered |