General
Property | Value | Comment |
---|---|---|
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
Property | Value | Comment |
---|---|---|
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 14.2 % Show Material materials with Elongation of 14.2 % | Predicted Value, A200 |
15.6 % Show Material materials with Elongation of 15.6 % | Predicted Value, A80 | |
18.4 % Show Material materials with Elongation of 18.4 % | Predicted Value, Transverse | |
20.1 % Show Material materials with Elongation of 20.1 % | Predicted Value, A80 Transverse | |
20.2 % Show Material materials with Elongation of 20.2 % | Predicted Value, A5 | |
21.0 % Show Material materials with Elongation of 21.0 % | Predicted Value, A50 | |
21.5 % Show Material materials with Elongation of 21.5 % | Predicted Value | |
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
Reduction of area | 41.2 % Show Material materials with Reduction of area of 41.2 % | Predicted Value |
43 % Show Material materials with Reduction of area of 43 % | Predicted Value, Transverse | |
Shear modulus | 82 GPa Show Material materials with Shear modulus of 82 GPa | Typical for Low Carbon Steel |
Shear strength | 515 MPa Show Material materials with Shear strength of 515 MPa | Predicted Value |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.32e-05 - 1.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
Max service temperature | 296.3 °C Show Material materials with Max service temperature of 296.3 °C | Predicted Value, Long |
500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Specific heat capacity | 465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 25 - 93 W/(m·K) Show Material materials with Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 7 S/m Show Material materials with Electrical conductivity of 7 S/m | Predicted Value |
Electrical resistivity | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value | Related Standards |
---|---|---|
Carbon | 0.21 % Show Material materials with Carbon of 0.21 % | ASTM A572 |
Manganese | 1.35 % Show Material materials with Manganese of 1.35 % | ASTM A572 |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % | ASTM A572 |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | ASTM A572 |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % | ASTM A572 |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |