ASTM A675 Grade 620 Hot-Wrought

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Ashby charts

See where ASTM A675 Grade 620 Hot-Wrought falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

7.8 g/cm³ at 23 °C

Typical for Steel

Mechanical

Elastic modulus

E

190 - 210 GPa at 23 °C

Show Unclassified Carbon Steel materials with Elastic modulus of 190 - 210 GPa at 23 °C

Typical for Steel

Elongation A200

A200

10 % at 23 °C

Show Unclassified Carbon Steel materials with Elongation A200 of 10 % at 23 °C

Elongation A50

A50

14 % at 23 °C

Show Unclassified Carbon Steel materials with Elongation A50 of 14 % at 23 °C

Poisson's ratio

ν

0.3 [-] at 23 °C

Show Unclassified Carbon Steel materials with Poisson's ratio of 0.3 [-] at 23 °C

Typical for Steel

Tensile strength

Rm

620 MPa at 23 °C

Show Unclassified Carbon Steel materials with Tensile strength of 620 MPa at 23 °C

Yield strength

YS

380 MPa at 23 °C

Show Unclassified Carbon Steel materials with Yield strength of 380 MPa at 23 °C

Chemical properties

Element

Weight %

Comment

Cu

0.2 %

S

0.05 %

P

0.04 %

This material data has been provided by ASTM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.