General
Property | Value | Comment |
---|---|---|
Density | 7.6 - 7.7 g/cm³ Show Material materials with Density of 7.6 - 7.7 g/cm³ | Typical for Martensitic Stainless Steel |
Mechanical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Elastic modulus | 220 GPa Show Material materials with Elastic modulus of 220 GPa | Typical for Martensitic Stainless Steel | |||
Elongation | 17.5 % Show Material materials with Elongation of 17.5 % | Predicted Value, A80 | |||
18 % Show Material materials with Elongation of 18 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | A200 | |
19.4 % Show Material materials with Elongation of 19.4 % | Predicted Value, Transverse | ||||
20.0 % Show Material materials with Elongation of 20.0 % | Predicted Value, A80 Transverse | ||||
22 % Show Material materials with Elongation of 22 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | A50 | |
24.7 % Show Material materials with Elongation of 24.7 % | Predicted Value | ||||
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel | |||
Reduction of area | 39.7 % Show Material materials with Reduction of area of 39.7 % | Predicted Value | |||
43.5 % Show Material materials with Reduction of area of 43.5 % | Predicted Value, Transverse | ||||
Shear modulus | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Martensitic Stainless Steel | |||
Shear strength | 516.5 MPa Show Material materials with Shear strength of 516.5 MPa | Predicted Value | |||
Tensile strength | 450 - 585 MPa Show Material materials with Tensile strength of 450 - 585 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | |
485 - 620 MPa Show Material materials with Tensile strength of 485 - 620 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | ||
Yield strength | 266.6 MPa Show Material materials with Yield strength of 266.6 MPa | Predicted Value, RP1 | |||
310 MPa Show Material materials with Yield strength of 310 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | ||
316.7 MPa Show Material materials with Yield strength of 316.7 MPa | Predicted Value, RP1 Transverse | ||||
345 MPa Show Material materials with Yield strength of 345 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | ||
353.7 MPa Show Material materials with Yield strength of 353.7 MPa | Predicted Value, Transverse | ||||
370.7 MPa Show Material materials with Yield strength of 370.7 MPa | Predicted Value, RP05 | ||||
371.3 MPa Show Material materials with Yield strength of 371.3 MPa | Predicted Value, RP02 | ||||
405.4 MPa Show Material materials with Yield strength of 405.4 MPa | Predicted Value, RP002 | ||||
454 MPa Show Material materials with Yield strength of 454 MPa | Predicted Value, RP02 Transverse |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1e-05 - 1.5e-05 1/K Show Material materials with Coefficient of thermal expansion of 1e-05 - 1.5e-05 1/K | Typical for Martensitic Stainless Steel |
Melting point | 1370 - 1530 °C Show Material materials with Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel |
Specific heat capacity | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | Typical for Martensitic Stainless Steel |
Thermal conductivity | 14 - 31 W/(m·K) Show Material materials with Thermal conductivity of 14 - 31 W/(m·K) | Typical for Martensitic Stainless Steel |
Electrical
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Carbon | 0.2 % Show Material materials with Carbon of 0.2 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Chromium | 0.25 % Show Material materials with Chromium of 0.25 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Copper | 0.35 % Show Material materials with Copper of 0.35 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Manganese | 0.7 - 1.35 % Show Material materials with Manganese of 0.7 - 1.35 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Molybdenum | 0.08 % Show Material materials with Molybdenum of 0.08 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Nickel | 0.25 % Show Material materials with Nickel of 0.25 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Niobium | 0.03 % Show Material materials with Niobium of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Silicon | 0.15 - 0.5 % Show Material materials with Silicon of 0.15 - 0.5 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Vanadium | 0.06 % Show Material materials with Vanadium of 0.06 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |