General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy | 20.0 °C | 20 J Show Material materials with Charpy impact energy of 20 J | |
Elastic modulus | 20.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation A200 | 20.0 °C | 15 % Show Material materials with Elongation A200 of 15 % | |
Elongation A50 | 20.0 °C | 17 % Show Material materials with Elongation A50 of 17 % | |
Poisson's ratio | 20.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 20.0 °C | 75 - 80 GPa Show Material materials with Shear modulus of 75 - 80 GPa | Typical for Carbon Steel |
Tensile strength | 20.0 °C | 550 MPa Show Material materials with Tensile strength of 550 MPa | |
Yield Strength Rp0.2, short transverse | 20.0 °C | 450 MPa Show Material materials with Yield Strength Rp0.2, short transverse of 450 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.32E-5 - 1.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 20.0 °C | 1.43E-7 - 1.74E-7 Ω·m Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
Property | Temperature | Value | Comment |
---|---|---|---|
Curie temperature | 20.0 °C | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value |
---|---|
Carbon | 0.2 % Show Material materials with Carbon of 0.2 % |
Chromium | 0.4 - 0.7 % Show Material materials with Chromium of 0.4 - 0.7 % |
Copper | 0.2 - 0.4 % Show Material materials with Copper of 0.2 - 0.4 % |
Manganese | 0.75 - 1.35 % Show Material materials with Manganese of 0.75 - 1.35 % |
Nickel | 0.5 % Show Material materials with Nickel of 0.5 % |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % |
Silicon | 0.15 - 0.5 % Show Material materials with Silicon of 0.15 - 0.5 % |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % |
Vanadium | 0.01 - 0.1 % Show Material materials with Vanadium of 0.01 - 0.1 % |