EN 10277-5 Grade C60R quenched and tempered and cold drawn (+QT+C)

.XLSX
.PDF
Save

Description

Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).,Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Related Standards

Equivalent Materials

Properties

General

Density ρ

7.85 g/cm³ at 20 °C

Mechanical

Elastic modulus E

210 GPa at 20 °C

Show chart

Elongation A

0 - 8 % at 20 °C

Shear modulus G

81 GPa at 20 °C

Tensile strength Rm

750 - 1100 MPa at 20 °C

Yield strength Rp0.2 Rp0.2

0 - 750 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

11.1 1/K at 100 °C

Show chart

Max service temperature, long Tmaxlong

-25 - 0 °C

Melting point Tm

1425 - 1478 °C

Typical for High Carbon Steel

Thermal conductivity λ

51 W/(m·K) at 20 °C

Show chart

Electrical

Electrical resistivity ρel

0.13 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Mn

0.6 - 0.9 %

C

0.57 - 0.65 %

S

0.02 - 0.04 %

Cr

0 - 0.4 %

Mo

0 - 0.1 %

More

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.