General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.82 g/cm³ Show Material materials with Density of 7.82 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa Show Material materials with Elastic modulus of 217 GPa | |
20.0 °C | 212 GPa Show Material materials with Elastic modulus of 212 GPa | ||
100.0 °C | 207 GPa Show Material materials with Elastic modulus of 207 GPa | ||
200.0 °C | 199 GPa Show Material materials with Elastic modulus of 199 GPa | ||
300.0 °C | 192 GPa Show Material materials with Elastic modulus of 192 GPa | ||
400.0 °C | 184 GPa Show Material materials with Elastic modulus of 184 GPa | ||
500.0 °C | 175 GPa Show Material materials with Elastic modulus of 175 GPa | ||
600.0 °C | 164 GPa Show Material materials with Elastic modulus of 164 GPa | ||
Elongation | 20.0 °C | 16 - 20 % Show Material materials with Elongation of 16 - 20 % | |
Elongation, transverse | 20.0 °C | 18 % Show Material materials with Elongation, transverse of 18 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa Show Material materials with Shear modulus of 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 500 - 550 MPa Show Material materials with Tensile strength of 500 - 550 MPa | |
Tensile strength, transverse | 20.0 °C | 500 MPa Show Material materials with Tensile strength, transverse of 500 MPa | |
Yield strength | 100.0 °C | 260 - 280 MPa Show Material materials with Yield strength of 260 - 280 MPa | |
200.0 °C | 245 - 265 MPa Show Material materials with Yield strength of 245 - 265 MPa | ||
250.0 °C | 226 - 235 MPa Show Material materials with Yield strength of 226 - 235 MPa | ||
300.0 °C | 216 - 226 MPa Show Material materials with Yield strength of 216 - 226 MPa | ||
350.0 °C | 196 - 206 MPa Show Material materials with Yield strength of 196 - 206 MPa | ||
Yield strength Rp0.2 | 20.0 °C | 300 - 400 MPa Show Material materials with Yield strength Rp0.2 of 300 - 400 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.08E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.08E-5 1/K | |
20.0 °C | 1.19E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.19E-5 1/K | ||
100.0 °C | 1.25E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.25E-5 1/K | ||
200.0 °C | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K | ||
300.0 °C | 1.36E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.36E-5 1/K | ||
400.0 °C | 1.41E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.41E-5 1/K | ||
500.0 °C | 1.45E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.45E-5 1/K | ||
600.0 °C | 1.49E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.49E-5 1/K | ||
Max service temperature | 500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) Show Material materials with Specific heat capacity of 423 J/(kg·K) | |
20.0 °C | 461 J/(kg·K) Show Material materials with Specific heat capacity of 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) Show Material materials with Specific heat capacity of 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) Show Material materials with Specific heat capacity of 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) Show Material materials with Specific heat capacity of 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) Show Material materials with Specific heat capacity of 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) Show Material materials with Specific heat capacity of 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) Show Material materials with Specific heat capacity of 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 39.6 W/(m·K) Show Material materials with Thermal conductivity of 39.6 W/(m·K) | |
100.0 °C | 41 W/(m·K) Show Material materials with Thermal conductivity of 41 W/(m·K) | ||
200.0 °C | 41 W/(m·K) Show Material materials with Thermal conductivity of 41 W/(m·K) | ||
300.0 °C | 39.9 W/(m·K) Show Material materials with Thermal conductivity of 39.9 W/(m·K) | ||
400.0 °C | 38.1 W/(m·K) Show Material materials with Thermal conductivity of 38.1 W/(m·K) | ||
500.0 °C | 35.9 W/(m·K) Show Material materials with Thermal conductivity of 35.9 W/(m·K) | ||
600.0 °C | 33.6 W/(m·K) Show Material materials with Thermal conductivity of 33.6 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 11 mm²/s Show Material materials with Thermal diffusivity of 11 mm²/s | |
100.0 °C | 10.6 mm²/s Show Material materials with Thermal diffusivity of 10.6 mm²/s | ||
200.0 °C | 9.9 mm²/s Show Material materials with Thermal diffusivity of 9.9 mm²/s | ||
300.0 °C | 9 mm²/s Show Material materials with Thermal diffusivity of 9 mm²/s | ||
400.0 °C | 8.1 mm²/s Show Material materials with Thermal diffusivity of 8.1 mm²/s | ||
500.0 °C | 6.9 mm²/s Show Material materials with Thermal diffusivity of 6.9 mm²/s | ||
600.0 °C | 5.7 mm²/s Show Material materials with Thermal diffusivity of 5.7 mm²/s | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 2.63E-7 Ω·m Show Material materials with Electrical resistivity of 2.63E-7 Ω·m |
100.0 °C | 3.12E-7 Ω·m Show Material materials with Electrical resistivity of 3.12E-7 Ω·m | |
200.0 °C | 3.85E-7 Ω·m Show Material materials with Electrical resistivity of 3.85E-7 Ω·m | |
300.0 °C | 4.7E-7 Ω·m Show Material materials with Electrical resistivity of 4.7E-7 Ω·m | |
400.0 °C | 5.71E-7 Ω·m Show Material materials with Electrical resistivity of 5.71E-7 Ω·m | |
500.0 °C | 6.88E-7 Ω·m Show Material materials with Electrical resistivity of 6.88E-7 Ω·m | |
600.0 °C | 8.25E-7 Ω·m Show Material materials with Electrical resistivity of 8.25E-7 Ω·m | |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % |
Carbon | 0.17 - 0.23 % Show Material materials with Carbon of 0.17 - 0.23 % |
Chromium | 0.4 % Show Material materials with Chromium of 0.4 % |
Manganese | 1 - 1.5 % Show Material materials with Manganese of 1 - 1.5 % |
Molybdenum | 0.1 % Show Material materials with Molybdenum of 0.1 % |
Nickel | 0.4 % Show Material materials with Nickel of 0.4 % |
Phosphorus | 0.04 % Show Material materials with Phosphorus of 0.04 % |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % |
Sulfur | 0.035 % Show Material materials with Sulfur of 0.035 % |