General
Property | Value | Comment |
---|---|---|
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
Property | Value | Related Standards | Shape | Comment |
---|---|---|---|---|
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel | ||
Elongation | 15.8 % Show Material materials with Elongation of 15.8 % | Predicted Value, A200 | ||
18.8 % Show Material materials with Elongation of 18.8 % | Predicted Value, A80 | |||
19.3 % Show Material materials with Elongation of 19.3 % | Predicted Value, Transverse | |||
19.9 % Show Material materials with Elongation of 19.9 % | Predicted Value, A80 Transverse | |||
21 % Show Material materials with Elongation of 21 % | ASTM A709 | Plate, Bar | A50 | |
23.9 % Show Material materials with Elongation of 23.9 % | Predicted Value | |||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel | ||
Reduction of area | 43.0 % Show Material materials with Reduction of area of 43.0 % | Predicted Value, Transverse | ||
44.2 % Show Material materials with Reduction of area of 44.2 % | Predicted Value | |||
Shear modulus | 82 GPa Show Material materials with Shear modulus of 82 GPa | Typical for Low Carbon Steel | ||
Shear strength | 506.1 MPa Show Material materials with Shear strength of 506.1 MPa | Predicted Value | ||
Tensile strength | 450 MPa Show Material materials with Tensile strength of 450 MPa | ASTM A709 | Plate, Bar |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.32e-05 - 1.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
Max service temperature | 298.3 °C Show Material materials with Max service temperature of 298.3 °C | Predicted Value, Long |
500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Specific heat capacity | 465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 25 - 93 W/(m·K) Show Material materials with Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 7 S/m Show Material materials with Electrical conductivity of 7 S/m | Predicted Value |
Electrical resistivity | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value | Related Standards | Shape |
---|---|---|---|
Carbon | 0.23 % Show Material materials with Carbon of 0.23 % | ASTM A709 | Plate, Bar |
Manganese | 1.35 % Show Material materials with Manganese of 1.35 % | ASTM A709 | Plate, Bar |
Niobium | 0.005 - 0.05 % Show Material materials with Niobium of 0.005 - 0.05 % | ASTM A709 | Plate, Bar |
Phosphorus | 0.03 % Show Material materials with Phosphorus of 0.03 % | ASTM A709 | Plate, Bar |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | ASTM A709 | Plate, Bar |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % | ASTM A709 | Plate, Bar |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |