Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 7.7 g/cm³ Show Material materials with Density of 7.7 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 200 GPa Show Material materials with Elastic modulus of 200 GPa at 23.0 °C | 23.0 °C | |
Elongation | 29 % Show Material materials with Elongation of 29 % at 23.0 °C | 23.0 °C | |
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] at 23.0 °C | 23.0 °C | Typical for Austenitic Stainless Steel |
Shear modulus | 77 GPa Show Material materials with Shear modulus of 77 GPa at 23.0 °C | 23.0 °C | Typical for Austenitic Stainless Steel |
Tensile strength | 990 MPa Show Material materials with Tensile strength of 990 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 590 MPa Show Material materials with Yield strength of 590 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K at 23.0 °C | 23.0 °C | |
Melting point | 1230 - 1480 °C Show Material materials with Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) at 23.0 °C | 23.0 °C | |
Thermal conductivity | 15 W/(m·K) Show Material materials with Thermal conductivity of 15 W/(m·K) at 23.0 °C | 23.0 °C |
Electrical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Electrical resistivity | 8.5E-7 Ω·m Show Material materials with Electrical resistivity of 8.5E-7 Ω·m at 23.0 °C | 23.0 °C | Typical for Austenitic Stainless Steel |
Chemical properties
| Property | ||
|---|---|---|
Carbon | 0 - 0.15 % | |
Chromium | 16 - 18 % | |
Iron | 67.5 - 75 % | |
Manganese | 5.5 - 7.5 % | |
Nickel | 3.5 - 5.5 % | |
Nitrogen | 0 - 0.25 % | |
Phosphorus | 0 - 0.06 % | |
Silicon | 0 - 1 % | |
Sulfur | 0 - 0.03 % |