Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 7.9 g/cm³ Show Material materials with Density of 7.9 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 200 GPa Show Material materials with Elastic modulus of 200 GPa at 23.0 °C | 23.0 °C | |
Elongation | 17 % Show Material materials with Elongation of 17 % at 23.0 °C | 23.0 °C | |
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] at 23.0 °C | 23.0 °C | Typical for Duplex Stainless Steel |
Shear modulus | 77 GPa Show Material materials with Shear modulus of 77 GPa at 23.0 °C | 23.0 °C | Typical for Duplex Stainless Steel |
Tensile strength | 870 MPa Show Material materials with Tensile strength of 870 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 610 MPa Show Material materials with Yield strength of 610 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 1.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-5 1/K at 23.0 °C | 23.0 °C | |
Max service temperature | 300 °C Show Material materials with Max service temperature of 300 °C | Typical for Duplex Stainless Steel | |
Melting point | 1375 - 1450 °C Show Material materials with Melting point of 1375 - 1450 °C | Typical for Duplex Stainless Steel | |
Specific heat capacity | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) at 23.0 °C | 23.0 °C | |
Thermal conductivity | 15 W/(m·K) Show Material materials with Thermal conductivity of 15 W/(m·K) at 23.0 °C | 23.0 °C |
Chemical properties
| Property | ||
|---|---|---|
Carbon | 0 - 0.03 % | |
Chromium | 24 - 26 % | |
Copper | 0 - 0.5 % | |
Iron | 58.1 - 66.8 % | |
Manganese | 0 - 2 % | |
Molybdenum | 3 - 5 % | |
Nickel | 6 - 8 % | |
Nitrogen | 0.24 - 0.35 % | |
Phosphorus | 0 - 0.04 % | |
Silicon | 0 - 1 % | |
Sulfur | 0 - 0.02 % |