AISI 304L Annealed

Want to keep this datasheet? Save it now in your required format

Description

Equivalent Materials

Ashby charts

See where AISI 304L Annealed falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

7.8 g/cm³ at 20 °C

Mechanical

Elastic modulus

E

200 GPa at 20 °C

Show Austenitic Stainless Steel materials with Elastic modulus of 200 GPa at 20 °C

Elongation

A

42 % at 20 °C

Show Austenitic Stainless Steel materials with Elongation of 42 % at 20 °C

Poisson's ratio

ν

0.3 [-] at 20 °C

Show Austenitic Stainless Steel materials with Poisson's ratio of 0.3 [-] at 20 °C

Typical for Austenitic Stainless Steel

Shear modulus

G

77 GPa at 20 °C

Show Austenitic Stainless Steel materials with Shear modulus of 77 GPa at 20 °C

Typical for Austenitic Stainless Steel

Tensile strength

Rm

550 MPa at 20 °C

Show Austenitic Stainless Steel materials with Tensile strength of 550 MPa at 20 °C

Yield strength

YS

200 MPa at 20 °C

Show Austenitic Stainless Steel materials with Yield strength of 200 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

1.7E-5 1/K at 20 °C

Melting point

Tm

1400 °C

Specific heat capacity

cp

500 J/(kg·K) at 20 °C

Thermal conductivity

λ

16 W/(m·K) at 20 °C

Electrical

Electrical resistivity

ρel

8.5E-7 Ω·m at 20 °C

Typical for Austenitic Stainless Steel

Chemical properties

Element

Weight %

Comment

Fe

64.8 - 74.5 %

Cr

17.5 - 20 %

Ni

8 - 12 %

C

0 - 0.03 %

Mn

0 - 2 %

More

This material data has been provided by MakeItFrom.com.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.