General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 210 GPa Show Material materials with Elastic modulus of 210 GPa | |
Elongation | 23.0 °C | 23 % Show Material materials with Elongation of 23 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Chromium Vanadium Steel |
Tensile strength | 23.0 °C | 670 MPa Show Material materials with Tensile strength of 670 MPa | |
Yield strength | 23.0 °C | 420 MPa Show Material materials with Yield strength of 420 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-5 1/K | |
Melting point | 1382 - 1529 °C Show Material materials with Melting point of 1382 - 1529 °C | Typical for Chromium Vanadium Steel | |
Specific heat capacity | 23.0 °C | 450 J/(kg·K) Show Material materials with Specific heat capacity of 450 J/(kg·K) |
Chemical properties
Property | Value |
---|---|
Carbon | 0.48 - 0.53 % Show Material materials with Carbon of 0.48 - 0.53 % |
Chromium | 0.8 - 1.1 % Show Material materials with Chromium of 0.8 - 1.1 % |
Iron | 96.7 - 97.7 % Show Material materials with Iron of 96.7 - 97.7 % |
Manganese | 0.7 - 0.9 % Show Material materials with Manganese of 0.7 - 0.9 % |
Phosphorus | 0 - 0.04 % Show Material materials with Phosphorus of 0 - 0.04 % |
Silicon | 0.15 - 0.35 % Show Material materials with Silicon of 0.15 - 0.35 % |
Sulfur | 0 - 0.04 % Show Material materials with Sulfur of 0 - 0.04 % |
Vanadium | 0.15 - 0.3 % Show Material materials with Vanadium of 0.15 - 0.3 % |