Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel | ||||
Elongation | 10.2 % Show Material materials with Elongation of 10.2 % | Predicted Value, A200 | ||||
11.2 % Show Material materials with Elongation of 11.2 % | Predicted Value, A80 | |||||
12.5 % Show Material materials with Elongation of 12.5 % | Predicted Value, Transverse | |||||
16.6 % Show Material materials with Elongation of 16.6 % | Predicted Value, A5 | |||||
16.8 % Show Material materials with Elongation of 16.8 % | Predicted Value, A50 | |||||
19.1 % Show Material materials with Elongation of 19.1 % | Predicted Value, A80 Transverse | |||||
20 °C | 14 % Show Material materials with Elongation of 14 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 15 % Show Material materials with Elongation of 15 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Hardness, Brinell | 252 [-] Show Material materials with Hardness, Brinell of 252 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel | ||||
Reduction of area | 43.0 % Show Material materials with Reduction of area of 43.0 % | Predicted Value, Transverse | ||||
20 °C | 55 % Show Material materials with Reduction of area of 55 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Shear modulus | 82 GPa Show Material materials with Shear modulus of 82 GPa | Typical for Low Carbon Steel | ||||
Shear strength | 502.3 MPa Show Material materials with Shear strength of 502.3 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 750 - 1050 MPa Show Material materials with Tensile strength of 750 - 1050 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | |
20 °C | 750 - 900 MPa Show Material materials with Tensile strength of 750 - 900 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 900 - 1050 MPa Show Material materials with Tensile strength of 900 - 1050 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 900 MPa Show Material materials with Tensile strength of 900 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
Yield strength | 305.9 MPa Show Material materials with Yield strength of 305.9 MPa | Predicted Value, RP05 | ||||
320.1 MPa Show Material materials with Yield strength of 320.1 MPa | Predicted Value, RP1 | |||||
325.6 MPa Show Material materials with Yield strength of 325.6 MPa | Predicted Value, RP1 Transverse | |||||
457.7 MPa Show Material materials with Yield strength of 457.7 MPa | Predicted Value, RP02 Transverse | |||||
466.6 MPa Show Material materials with Yield strength of 466.6 MPa | Predicted Value, Transverse | |||||
640.2 MPa Show Material materials with Yield strength of 640.2 MPa | Predicted Value, RP02 | |||||
709.8 MPa Show Material materials with Yield strength of 709.8 MPa | Predicted Value, RP002 | |||||
20 °C | 600 MPa Show Material materials with Yield strength of 600 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat | ||
20 °C | 700 MPa Show Material materials with Yield strength of 700 MPa | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.32e-05 - 1.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
Max service temperature | 328.7 °C Show Material materials with Max service temperature of 328.7 °C | Predicted Value, Long |
500 °C Show Material materials with Max service temperature of 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Specific heat capacity | 465 J/(kg·K) Show Material materials with Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 25 - 93 W/(m·K) Show Material materials with Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 7 S/m Show Material materials with Electrical conductivity of 7 S/m | Predicted Value |
Electrical resistivity | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Boron | 0.0008 - 0.005 % Show Material materials with Boron of 0.0008 - 0.005 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
0.001 - 0.005 % Show Material materials with Boron of 0.001 - 0.005 % | quenched and tempered (+QT) | EN 10083-3, ISO 683-2 | Bar, Forging, Sheet, Strip, Flat | |
Carbon | 0.17 - 0.23 % Show Material materials with Carbon of 0.17 - 0.23 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Copper | 0.4 % Show Material materials with Copper of 0.4 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Manganese | 1.1 - 1.4 % Show Material materials with Manganese of 1.1 - 1.4 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Phosphorus | 0.025 % Show Material materials with Phosphorus of 0.025 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |
Sulfur | 0.035 % Show Material materials with Sulfur of 0.035 % | quenched and tempered (+QT) | ISO 683-2, EN 10083-3 | Bar, Forging, Sheet, Strip, Flat |