Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ | Typical for Steel |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 190 - 210 GPa Show Material materials with Elastic modulus of 190 - 210 GPa | Typical for Steel | ||||
Elongation | 13.0 % Show Material materials with Elongation of 13.0 % | Predicted Value, A200 | ||||
13.2 % Show Material materials with Elongation of 13.2 % | Predicted Value, Transverse | |||||
17.5 % Show Material materials with Elongation of 17.5 % | Predicted Value, A50 | |||||
17.5 % Show Material materials with Elongation of 17.5 % | Predicted Value, A80 Transverse | |||||
18.3 % Show Material materials with Elongation of 18.3 % | Predicted Value, A5 | |||||
20 °C | 10 % Show Material materials with Elongation of 10 % | thermomechanically rolled | EN 10149-2 | Flat | A80 | |
20 °C | 10 % Show Material materials with Elongation of 10 % | thermomechanically rolled | EN 10149-2 | Flat | ||
20 °C | 12 % Show Material materials with Elongation of 12 % | thermomechanically rolled | EN 10149-2 | Flat | A80 | |
20 °C | 12 % Show Material materials with Elongation of 12 % | thermomechanically rolled | EN 10149-2 | Flat | ||
Hardness, Brinell | 248 [-] Show Material materials with Hardness, Brinell of 248 [-] | Predicted Value, Transverse | ||||
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Steel | ||||
Reduction of area | 38.9 % Show Material materials with Reduction of area of 38.9 % | Predicted Value | ||||
44.1 % Show Material materials with Reduction of area of 44.1 % | Predicted Value, Transverse | |||||
Shear modulus | 80.1 GPa Show Material materials with Shear modulus of 80.1 GPa | Predicted Value | ||||
Shear strength | 583.8 MPa Show Material materials with Shear strength of 583.8 MPa | Predicted Value | ||||
Tensile strength | 20 °C | 700 - 880 MPa Show Material materials with Tensile strength of 700 - 880 MPa | thermomechanically rolled | EN 10149-2 | Flat | |
Yield strength | 293.5 MPa Show Material materials with Yield strength of 293.5 MPa | Predicted Value, RP1 | ||||
328.8 MPa Show Material materials with Yield strength of 328.8 MPa | Predicted Value, RP1 Transverse | |||||
505.4 MPa Show Material materials with Yield strength of 505.4 MPa | Predicted Value, RP02 Transverse | |||||
525.6 MPa Show Material materials with Yield strength of 525.6 MPa | Predicted Value, Transverse | |||||
547.5 MPa Show Material materials with Yield strength of 547.5 MPa | Predicted Value, RP05 | |||||
562.8 MPa Show Material materials with Yield strength of 562.8 MPa | Predicted Value, RP02 | |||||
623.6 MPa Show Material materials with Yield strength of 623.6 MPa | Predicted Value, RP002 | |||||
20 °C | 650 MPa Show Material materials with Yield strength of 650 MPa | thermomechanically rolled | EN 10149-2 | Flat |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 11.96 1/K Show Material materials with Coefficient of thermal expansion of 11.96 1/K | Predicted Value |
Specific heat capacity | 453.9 J/(kg·K) Show Material materials with Specific heat capacity of 453.9 J/(kg·K) | Predicted Value |
Thermal conductivity | 37.64 W/(m·K) Show Material materials with Thermal conductivity of 37.64 W/(m·K) | Predicted Value |
Electrical
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 0.015 % Show Material materials with Aluminium of 0.015 % | thermomechanically rolled | EN 10149-2 | Flat |
Boron | 0.005 % Show Material materials with Boron of 0.005 % | thermomechanically rolled | EN 10149-2 | Flat |
Carbon | 0.12 % Show Material materials with Carbon of 0.12 % | thermomechanically rolled | EN 10149-2 | Flat |
Manganese | 2 % Show Material materials with Manganese of 2 % | thermomechanically rolled | EN 10149-2 | Flat |
Molybdenum | 0.5 % Show Material materials with Molybdenum of 0.5 % | thermomechanically rolled | EN 10149-2 | Flat |
Niobium | 0.09 % Show Material materials with Niobium of 0.09 % | thermomechanically rolled | EN 10149-2 | Flat |
Phosphorus | 0.025 % Show Material materials with Phosphorus of 0.025 % | thermomechanically rolled | EN 10149-2 | Flat |
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % | thermomechanically rolled | EN 10149-2 | Flat |
Sulfur | 0.015 % Show Material materials with Sulfur of 0.015 % | thermomechanically rolled | EN 10149-2 | Flat |
Titanium | 0.22 % Show Material materials with Titanium of 0.22 % | thermomechanically rolled | EN 10149-2 | Flat |
Vanadium | 0.2 % Show Material materials with Vanadium of 0.2 % | thermomechanically rolled | EN 10149-2 | Flat |