EN 10130 Grade DC03 skin passed

Want to keep this datasheet? Save it now in your required format


The non-alloy steel DC03 acc. to DIN EN 10130 is suitable for cold forming of simple profile forms and components. Mechanical foldings are possible for thicknesses of up to 1,5 mm. To freedom of stretcher strains applies a period of 3 months after provision of the products for surface type A and B. Welding: DC03 is weldable by the following welding methods: MAG (metal-active-gas), plasma welding, laser welding, compression weld welding, resistance welding (spot, roll weld, buckle welding), arc welding. The steel acts as substrate for surface refined and coated bands and sheets. Application of DC03: household appliances industry, construction trade, car manufacturing, traffic system. Acc. to DIN EN 10139 DC03 is offered as cold rolled band or bar, cut in strength range HK270 to HK590. On welding of DC03 in condition HK290 to HK590 has to be considered the potential influence to the mechanical properties

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

7.8 - 7.9 g/cm³

Show Material materials with Density of 7.8 - 7.9 g/cm³

Typical for Low Carbon Steel



Elastic modulus

23.0 °C

200 - 215 GPa

Show Material materials with Elastic modulus of 200 - 215 GPa

Typical for Low Carbon Steel

Elongation A80

20.0 °C

34 %

Show Material materials with Elongation A80 of 34 %

Poisson's ratio

23.0 °C

0.29 [-]

Show Material materials with Poisson's ratio of 0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Show Material materials with Shear modulus of 82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

270 - 370 MPa

Show Material materials with Tensile strength of 270 - 370 MPa

Yield strength

20.0 °C

140 - 240 MPa

Show Material materials with Yield strength of 140 - 240 MPa



Coefficient of thermal expansion

23.0 °C

1.32E-5 - 1.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K

Typical for Low Carbon Steel

Max service temperature

500 °C

Show Material materials with Max service temperature of 500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Show Material materials with Melting point of 1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

23.0 °C

465 J/(kg·K)

Show Material materials with Specific heat capacity of 465 J/(kg·K)

Typical for Low Carbon Steel

Thermal conductivity

23.0 °C

25 - 93 W/(m·K)

Show Material materials with Thermal conductivity of 25 - 93 W/(m·K)

Typical for Low Carbon Steel



Electrical resistivity

23.0 °C

1.43E-7 - 1.74E-7 Ω·m

Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m

Typical for Carbon Steel



Curie temperature

770 °C

Show Material materials with Curie temperature of 770 °C

Typical for Low Carbon Steel

Chemical properties



0.1 %

Show Material materials with Carbon of 0.1 %


0.45 %

Show Material materials with Manganese of 0.45 %


0.04 %

Show Material materials with Phosphorus of 0.04 %


0.035 %

Show Material materials with Sulfur of 0.035 %