EN 10152 Grade DC05 skin passed

Want to keep this datasheet? Save it now in your required format


The non-alloy, electrolytically galvanized steel DC05+ZE is suitable as special deep drawing quality for cold forming of complexest profile forms, construction components and molded parts. For freedom from stretcher strains applies a term of 6 months after provision of the products for surface type A and B. The same applies for valid time of mechanical properties: The following zinc platings are available (double-sided): ZE 25/25 (nominal zinc plating 2,5 µm equivalent 18 g/m²) ZE 50/50 (nominal zinc plating 5,0 µm equivalent 36 g/m²) ZE 75/75 (nominal zinc plating 7,5 µm equivalent 54 g/m²) ZE 100/100 (zinc plating 10 µm equivalent 72 g/m²) Differentially galvanized band is available by agreement. Following surface conditions are possible: P...phosphated PC...phosphated and chemical treated C...chemical passivated PCO...phosphated, chemical treated and oiled CO...chemical passivated and oiled PO...phosphated and oiled O...oiled S...sealed U...without surface treatment Application of DC05 + ZE: car manufacturing, traffic engineering, construction trade

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

7.8 - 7.9 g/cm³

Show Material materials with Density of 7.8 - 7.9 g/cm³

Typical for Low Carbon Steel



Elastic modulus

23.0 °C

200 - 215 GPa

Show Material materials with Elastic modulus of 200 - 215 GPa

Typical for Low Carbon Steel

Elongation A80

20.0 °C

39 %

Show Material materials with Elongation A80 of 39 %

Elongation A80, transverse

20.0 °C

35 - 39 %

Show Material materials with Elongation A80, transverse of 35 - 39 %

Poisson's ratio

23.0 °C

0.29 [-]

Show Material materials with Poisson's ratio of 0.29 [-]

Typical for Low Carbon Steel

Shear modulus

23.0 °C

82 GPa

Show Material materials with Shear modulus of 82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

270 - 330 MPa

Show Material materials with Tensile strength of 270 - 330 MPa

Tensile strength, transverse

20.0 °C

270 - 330 MPa

Show Material materials with Tensile strength, transverse of 270 - 330 MPa

Yield strength

20.0 °C

140 - 190 MPa

Show Material materials with Yield strength of 140 - 190 MPa

Yield strength, transverse

20.0 °C

140 - 240 MPa

Show Material materials with Yield strength, transverse of 140 - 240 MPa



Coefficient of thermal expansion

23.0 °C

1.32E-5 - 1.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K

Typical for Low Carbon Steel

Max service temperature

500 °C

Show Material materials with Max service temperature of 500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Show Material materials with Melting point of 1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

23.0 °C

465 J/(kg·K)

Show Material materials with Specific heat capacity of 465 J/(kg·K)

Typical for Low Carbon Steel

Thermal conductivity

23.0 °C

25 - 93 W/(m·K)

Show Material materials with Thermal conductivity of 25 - 93 W/(m·K)

Typical for Low Carbon Steel



Electrical resistivity

23.0 °C

1.43E-7 - 1.74E-7 Ω·m

Show Material materials with Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m

Typical for Carbon Steel



Curie temperature

770 °C

Show Material materials with Curie temperature of 770 °C

Typical for Low Carbon Steel

Chemical properties



0.06 %

Show Material materials with Carbon of 0.06 %


0.35 %

Show Material materials with Manganese of 0.35 %


0.03 %

Show Material materials with Phosphorus of 0.03 %


0.025 %

Show Material materials with Sulfur of 0.025 %