ISO 683-4 Grade 35SPb20 quenched and tempered (+QT)

Want to keep this datasheet? Save it now in your required format

Description

The free-cutting steel 35SPb20, suitable for quenching and tempering, is used for bulk parts of mean strength, especially for lower requirements to ductility in transversal direction opposite to comparable C-steels (e.g. C35). Machinability enhancement is achievable by Pb-content. Application in automotive engineering, as well as in apparatus equipment and machine engineering (e.g. screws, nuts, small-size parts).

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Show Material materials with Density of 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

210 GPa

Show Material materials with Elastic modulus of 210 GPa

200.0 °C

193 GPa

Show Material materials with Elastic modulus of 193 GPa

300.0 °C

185 GPa

Show Material materials with Elastic modulus of 185 GPa

400.0 °C

175 GPa

Show Material materials with Elastic modulus of 175 GPa

Elongation

20.0 °C

15 - 17 %

Show Material materials with Elongation of 15 - 17 %

Poisson's ratio

23.0 °C

0.29 [-]

Show Material materials with Poisson's ratio of 0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

20.0 °C

81 GPa

Show Material materials with Shear modulus of 81 GPa

Tensile strength

20.0 °C

550 - 780 MPa

Show Material materials with Tensile strength of 550 - 780 MPa

Yield strength

20.0 °C

320 - 430 MPa

Show Material materials with Yield strength of 320 - 430 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.1E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.1E-5 1/K

200.0 °C

1.18E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.18E-5 1/K

400.0 °C

1.32E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.32E-5 1/K

Unlock all property charts

Max service temperature

500 °C

Show Material materials with Max service temperature of 500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Show Material materials with Melting point of 1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

20.0 °C

420 J/(kg·K)

Show Material materials with Specific heat capacity of 420 J/(kg·K)

100.0 °C

490 J/(kg·K)

Show Material materials with Specific heat capacity of 490 J/(kg·K)

200.0 °C

530 J/(kg·K)

Show Material materials with Specific heat capacity of 530 J/(kg·K)

400.0 °C

610 J/(kg·K)

Show Material materials with Specific heat capacity of 610 J/(kg·K)

Unlock all property charts

Thermal conductivity

20.0 °C

49 W/(m·K)

Show Material materials with Thermal conductivity of 49 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 Ω·m

Show Material materials with Electrical resistivity of 1.2E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.32 - 0.39 %

Show Material materials with Carbon of 0.32 - 0.39 %

Lead

0.15 - 0.35 %

Show Material materials with Lead of 0.15 - 0.35 %

Manganese

0.7 - 1.1 %

Show Material materials with Manganese of 0.7 - 1.1 %

Phosphorus

0.06 %

Show Material materials with Phosphorus of 0.06 %

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

Sulfur

0.15 - 0.25 %

Show Material materials with Sulfur of 0.15 - 0.25 %