General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.7 - 7.71 g/cm³ Show Material materials with Density of 7.7 - 7.71 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 216 - 222 GPa Show Material materials with Elastic modulus of 216 - 222 GPa | |
100.0 °C | 213 - 216 GPa Show Material materials with Elastic modulus of 213 - 216 GPa | ||
200.0 °C | 207 - 209 GPa Show Material materials with Elastic modulus of 207 - 209 GPa | ||
300.0 °C | 200 - 201 GPa Show Material materials with Elastic modulus of 200 - 201 GPa | ||
400.0 °C | 192 GPa Show Material materials with Elastic modulus of 192 GPa | ||
500.0 °C | 183 GPa Show Material materials with Elastic modulus of 183 GPa | ||
600.0 °C | 174 GPa Show Material materials with Elastic modulus of 174 GPa | ||
Elongation | 20.0 °C | 12 - 15 % Show Material materials with Elongation of 12 - 15 % | |
Elongation, transverse | 20.0 °C | 11 % Show Material materials with Elongation, transverse of 11 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 20.0 °C | 650 - 800 MPa Show Material materials with Tensile strength of 650 - 800 MPa | |
Tensile strength, transverse | 20.0 °C | 650 - 800 MPa Show Material materials with Tensile strength, transverse of 650 - 800 MPa | |
Yield strength Rp0.2 | 20.0 °C | 450 MPa Show Material materials with Yield strength Rp0.2 of 450 MPa | |
Yield strength Rp0.2, transverse | 20.0 °C | 450 MPa Show Material materials with Yield strength Rp0.2, transverse of 450 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.02E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.02E-5 1/K | |
100.0 °C | 1.05E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.05E-5 1/K | ||
200.0 °C | 1.09E-5 - 1.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.09E-5 - 1.1E-5 1/K | ||
300.0 °C | 1.13E-5 - 1.15E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.13E-5 - 1.15E-5 1/K | ||
400.0 °C | 1.16E-5 - 1.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.16E-5 - 1.2E-5 1/K | ||
500.0 °C | 1.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-5 1/K | ||
600.0 °C | 1.22E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.22E-5 1/K | ||
Max service temperature, long | -40 - 550 °C Show Material materials with Max service temperature, long of -40 - 550 °C | ||
Melting point | 1370 - 1530 °C Show Material materials with Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 439 - 460 J/(kg·K) Show Material materials with Specific heat capacity of 439 - 460 J/(kg·K) | |
100.0 °C | 474 J/(kg·K) Show Material materials with Specific heat capacity of 474 J/(kg·K) | ||
200.0 °C | 498 J/(kg·K) Show Material materials with Specific heat capacity of 498 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) Show Material materials with Specific heat capacity of 517 J/(kg·K) | ||
400.0 °C | 538 J/(kg·K) Show Material materials with Specific heat capacity of 538 J/(kg·K) | ||
500.0 °C | 564 J/(kg·K) Show Material materials with Specific heat capacity of 564 J/(kg·K) | ||
600.0 °C | 598 J/(kg·K) Show Material materials with Specific heat capacity of 598 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 24.6 - 30 W/(m·K) Show Material materials with Thermal conductivity of 24.6 - 30 W/(m·K) | |
100.0 °C | 24.7 W/(m·K) Show Material materials with Thermal conductivity of 24.7 W/(m·K) | ||
200.0 °C | 25 W/(m·K) Show Material materials with Thermal conductivity of 25 W/(m·K) | ||
300.0 °C | 25.2 W/(m·K) Show Material materials with Thermal conductivity of 25.2 W/(m·K) | ||
400.0 °C | 25.5 W/(m·K) Show Material materials with Thermal conductivity of 25.5 W/(m·K) | ||
500.0 °C | 25.8 W/(m·K) Show Material materials with Thermal conductivity of 25.8 W/(m·K) | ||
600.0 °C | 26 W/(m·K) Show Material materials with Thermal conductivity of 26 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 7.3 mm²/s Show Material materials with Thermal diffusivity of 7.3 mm²/s | |
100.0 °C | 6.4 mm²/s Show Material materials with Thermal diffusivity of 6.4 mm²/s | ||
200.0 °C | 6.1 mm²/s Show Material materials with Thermal diffusivity of 6.1 mm²/s | ||
300.0 °C | 5.8 mm²/s Show Material materials with Thermal diffusivity of 5.8 mm²/s | ||
400.0 °C | 5.4 mm²/s Show Material materials with Thermal diffusivity of 5.4 mm²/s | ||
500.0 °C | 4.8 mm²/s Show Material materials with Thermal diffusivity of 4.8 mm²/s | ||
600.0 °C | 4.1 mm²/s Show Material materials with Thermal diffusivity of 4.1 mm²/s | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 5.87E-7 - 6E-7 Ω·m Show Material materials with Electrical resistivity of 5.87E-7 - 6E-7 Ω·m |
100.0 °C | 6.55E-7 Ω·m Show Material materials with Electrical resistivity of 6.55E-7 Ω·m | |
200.0 °C | 7.38E-7 Ω·m Show Material materials with Electrical resistivity of 7.38E-7 Ω·m | |
300.0 °C | 8.19E-7 Ω·m Show Material materials with Electrical resistivity of 8.19E-7 Ω·m | |
400.0 °C | 8.96E-7 Ω·m Show Material materials with Electrical resistivity of 8.96E-7 Ω·m | |
500.0 °C | 9.7E-7 Ω·m Show Material materials with Electrical resistivity of 9.7E-7 Ω·m | |
600.0 °C | 1.04E-6 Ω·m Show Material materials with Electrical resistivity of 1.04E-6 Ω·m | |
Chemical properties
Property | Value |
---|---|
Carbon | 0.17 - 0.25 % Show Material materials with Carbon of 0.17 - 0.25 % |
Chromium | 12 - 14 % Show Material materials with Chromium of 12 - 14 % |
Manganese | 1 % Show Material materials with Manganese of 1 % |
Phosphorus | 0.05 % Show Material materials with Phosphorus of 0.05 % |
Silicon | 1 % Show Material materials with Silicon of 1 % |
Sulfur | 0.03 % Show Material materials with Sulfur of 0.03 % |