Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.65 - 7.7 g/cm³ Show Material materials with Density of 7.65 - 7.7 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 196 - 215 GPa Show Material materials with Elastic modulus of 196 - 215 GPa | |
100.0 °C | 212 GPa Show Material materials with Elastic modulus of 212 GPa | ||
200.0 °C | 205 GPa Show Material materials with Elastic modulus of 205 GPa | ||
300.0 °C | 200 GPa Show Material materials with Elastic modulus of 200 GPa | ||
400.0 °C | 190 GPa Show Material materials with Elastic modulus of 190 GPa | ||
Elongation | 20.0 °C | 10 - 14 % Show Material materials with Elongation of 10 - 14 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Martensitic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 20.0 °C | 900 - 1050 MPa Show Material materials with Tensile strength of 900 - 1050 MPa | |
Yield strength Rp0.2 | 20.0 °C | 700 MPa Show Material materials with Yield strength Rp0.2 of 700 MPa | |
100.0 °C | 565 MPa Show Material materials with Yield strength Rp0.2 of 565 MPa | ||
150.0 °C | 525 MPa Show Material materials with Yield strength Rp0.2 of 525 MPa | ||
200.0 °C | 505 MPa Show Material materials with Yield strength Rp0.2 of 505 MPa | ||
250.0 °C | 490 MPa Show Material materials with Yield strength Rp0.2 of 490 MPa | ||
300.0 °C | 470 MPa Show Material materials with Yield strength Rp0.2 of 470 MPa | ||
350.0 °C | 430 MPa Show Material materials with Yield strength Rp0.2 of 430 MPa | ||
400.0 °C | 375 MPa Show Material materials with Yield strength Rp0.2 of 375 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 9.2E-6 1/K Show Material materials with Coefficient of thermal expansion of 9.2E-6 1/K | |
20.0 °C | 9.9E-6 1/K Show Material materials with Coefficient of thermal expansion of 9.9E-6 1/K | ||
100.0 °C | 1E-5 - 1.03E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.03E-5 1/K | ||
200.0 °C | 1.05E-5 - 1.08E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.05E-5 - 1.08E-5 1/K | ||
300.0 °C | 1.05E-5 - 1.12E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.05E-5 - 1.12E-5 1/K | ||
400.0 °C | 1.05E-5 - 1.16E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.05E-5 - 1.16E-5 1/K | ||
500.0 °C | 1.19E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.19E-5 1/K | ||
600.0 °C | 1.21E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.21E-5 1/K | ||
700.0 °C | 1.24E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.24E-5 1/K | ||
800.0 °C | 1.29E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.29E-5 1/K | ||
900.0 °C | 1.34E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.34E-5 1/K | ||
1000.0 °C | 1.39E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.39E-5 1/K | ||
Melting point | 1370 - 1530 °C Show Material materials with Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 450 - 460 J/(kg·K) Show Material materials with Specific heat capacity of 450 - 460 J/(kg·K) | |
100.0 °C | 482 J/(kg·K) Show Material materials with Specific heat capacity of 482 J/(kg·K) | ||
200.0 °C | 506 J/(kg·K) Show Material materials with Specific heat capacity of 506 J/(kg·K) | ||
300.0 °C | 525 J/(kg·K) Show Material materials with Specific heat capacity of 525 J/(kg·K) | ||
400.0 °C | 547 J/(kg·K) Show Material materials with Specific heat capacity of 547 J/(kg·K) | ||
500.0 °C | 576 J/(kg·K) Show Material materials with Specific heat capacity of 576 J/(kg·K) | ||
600.0 °C | 616 J/(kg·K) Show Material materials with Specific heat capacity of 616 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 19.6 - 25 W/(m·K) Show Material materials with Thermal conductivity of 19.6 - 25 W/(m·K) | |
Thermal diffusivity | 20.0 °C | 5.7 mm²/s Show Material materials with Thermal diffusivity of 5.7 mm²/s | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 6.17E-7 - 7E-7 Ω·m Show Material materials with Electrical resistivity of 6.17E-7 - 7E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.12 - 0.22 % Show Material materials with Carbon of 0.12 - 0.22 % |
Chromium | 15 - 17 % Show Material materials with Chromium of 15 - 17 % |
Manganese | 1.5 % Show Material materials with Manganese of 1.5 % |
Nickel | 1.5 - 2.5 % Show Material materials with Nickel of 1.5 - 2.5 % |
Phosphorus | 0.04 % Show Material materials with Phosphorus of 0.04 % |
Silicon | 1 % Show Material materials with Silicon of 1 % |
Sulfur | 0.015 - 0.03 % Show Material materials with Sulfur of 0.015 - 0.03 % |