EN 10277-3 Grade 44SMn28 cold drawn

Want to keep this datasheet? Save it now in your required format

Description

The free cutting case hardening steel 44SMn28 is well machinable and used for production of turned parts of higher strength demands. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Related Standards

EN 10277-3

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³	Typical for Manganese Steel

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa	Typical for Manganese Steel
Elongation	20.0 °C	5 - 7 % Show Material materials with Elongation of 5 - 7 %
Poisson's ratio	23.0 °C	0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-]	Typical for Manganese Steel
Tensile strength	20.0 °C	630 - 1030 MPa Show Material materials with Tensile strength of 630 - 1030 MPa
Yield strength Rp0.2	20.0 °C	390 - 600 MPa Show Material materials with Yield strength Rp0.2 of 390 - 600 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.33E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.33E-5 1/K	Typical for Manganese Steel
Melting point		1382 - 1529 °C Show Material materials with Melting point of 1382 - 1529 °C	Typical for Manganese Steel
Specific heat capacity	23.0 °C	510 - 553 J/(kg·K) Show Material materials with Specific heat capacity of 510 - 553 J/(kg·K)	Typical for Manganese Steel
Thermal conductivity	23.0 °C	14 - 16 W/(m·K) Show Material materials with Thermal conductivity of 14 - 16 W/(m·K)	Typical for Manganese Steel

Chemical properties

Property	Value
Carbon	0.4 - 0.48 % Show Material materials with Carbon of 0.4 - 0.48 %
Manganese	1.3 - 1.7 % Show Material materials with Manganese of 1.3 - 1.7 %
Phosphorus	0.06 % Show Material materials with Phosphorus of 0.06 %
Silicon	0.4 % Show Material materials with Silicon of 0.4 %
Sulfur	0.24 - 0.33 % Show Material materials with Sulfur of 0.24 - 0.33 %