General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 200 - 215 GPa Show Material materials with Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation A80, transverse | 20.0 °C | 34 % Show Material materials with Elongation A80, transverse of 34 % | |
Poisson's ratio | 20.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
Tensile strength, transverse | 20.0 °C | 290 - 360 MPa Show Material materials with Tensile strength, transverse of 290 - 360 MPa | |
Yield strength Rp0.2, transverse | 20.0 °C | 180 - 240 MPa Show Material materials with Yield strength Rp0.2, transverse of 180 - 240 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 1.32E-5 - 1.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Melting point | 1480 - 1526 °C Show Material materials with Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
Magnetic
Property | Value | Comment |
---|---|---|
Curie temperature | 770 °C Show Material materials with Curie temperature of 770 °C | Typical for Low Carbon Steel |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.02 % Show Material materials with Aluminium of 0.02 % |
Carbon | 0.04 - 0.1 % Show Material materials with Carbon of 0.04 - 0.1 % |
Manganese | 0.7 % Show Material materials with Manganese of 0.7 % |
Niobium | 0.09 % Show Material materials with Niobium of 0.09 % |
Phosphorus | 0.06 % Show Material materials with Phosphorus of 0.06 % |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % |
Sulfur | 0.025 % Show Material materials with Sulfur of 0.025 % |
Titanium | 0.12 % Show Material materials with Titanium of 0.12 % |