EN 10292 Grade HX260BD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated

Want to keep this datasheet? Save it now in your required format

Description

The steel HX260BD (X=roll condition, B=bake hardening, D=hot-dip coatable) is producible with the following coatings: - HX260BD+Z (plating Zn) with coating weights (double-sided) of 100, 140, 200, 225 and 275 g/m² (100 g approximate 7,1 µm per side) - HX260BD+ZF (plating Zn-Fe) with coating weights (double-sided) of 100 and 120 g/m² (100 g approximate 7,1 µm per side) - HX260BD+ZA (plating Zn-Al) with coating weights (double-sided) of 095, 130, 185, 200 and 255 g/m² (95 g approximate 7,2 µm per side) - HX260BD+AZ (plating Al-Zn) with coating weights (double-sided) of 100, 150 and 185 g/m² (100 g approximate 13,3 µm per side) - HX260BD+AS (plating Al-Si) with coating weights (double-sided) of 060 and 080 g/m² (100 g approximate 17 µm per side) The hot dip galvanizing refined flat products are available by arrangement on ordering with different coating weights (also per side). Following surface protection types can be delivered: chemical passivated, oiled, chemical passivated and oiled, sealed, phosphated, phosphated and oiled. Mechanical properties are warranted for a period of 3 months for Bake-hardening steels and for a period of 6 months after provision of the products for all other sorts. The same terms are valid for freedom from stretcher strains (surface type B and C). It is suitable for usual welding methods. For higher coating weights on welding are where approppriate necessary special measures. Furthermore suitability for joining by sticking as well as for application of organic coatings. Application: household appliances industry, construction trade, electrical industry, furniture industry, car industry.,The steel HX260BD (X=roll condition, B=bake hardening, D=hot-dip coatable) is deliverable with the following coatings: - HX260BD+Z (plating Zn) with coating weights (double-sided) of 100, 140, 200, 225 and 275 g/m² (100 g approximate 7,1 µm per side) - HX260BD+ZF (plating Zn-Fe) with coating weights (double-sided) of 100 and 120 g/m² (100 g approximate 7,1 µm per side) - HX260BD+ZA (plating Zn-Al) with coating weights (double-sided) of 095, 130, 185, 200 and 255 g/m² (95 g approximate 7,2 µm per side) - HX260BD+AZ (plating Al-Zn) with coating weights (double-sided) of 100, 150 and 185 g/m² (100 g approximate 13,3 µm per side) - HX260BD+AS (plating Al-Si) with coating weights (double-sided) of 060 and 080 g/m² (100 g approximate 17 µm per side) The hot dip galvanizing refined flat products are available by arrangement on ordering with different coating weights (also per side). Following surface protection types can be delivered: chemical passivated, oiled, chemical passivated and oiled, sealed, phosphated, phosphated and oiled. Mechanical properties are warranted for a period of 3 months after provision. The same time is valid for freedom from stretcher strains (surface type B and C). It is suitable for usual welding methods. For higher coating weights on welding are where approppriate necessary special measures. Furthermore suitability for joining by sticking as well as for application of organic coatings. Application: household appliances industry, construction trade, electrical industry, furniture industry, car industry.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

20.0 °C

7.8 - 7.9 g/cm³

Show Material materials with Density of 7.8 - 7.9 g/cm³

Typical for Manganese Steel

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

200 - 215 GPa

Show Material materials with Elastic modulus of 200 - 215 GPa

Typical for Manganese Steel

Elongation A80, transverse

20.0 °C

28 %

Show Material materials with Elongation A80, transverse of 28 %

Poisson's ratio

20.0 °C

0.29 [-]

Show Material materials with Poisson's ratio of 0.29 [-]

Typical for Manganese Steel

Tensile strength, transverse

20.0 °C

360 - 440 MPa

Show Material materials with Tensile strength, transverse of 360 - 440 MPa

Yield strength Rp0.2, transverse

20.0 °C

260 - 320 MPa

Show Material materials with Yield strength Rp0.2, transverse of 260 - 320 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.33E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.33E-5 1/K

Typical for Manganese Steel

Melting point

1382 - 1529 °C

Show Material materials with Melting point of 1382 - 1529 °C

Typical for Manganese Steel

Specific heat capacity

20.0 °C

510 - 553 J/(kg·K)

Show Material materials with Specific heat capacity of 510 - 553 J/(kg·K)

Typical for Manganese Steel

Thermal conductivity

20.0 °C

14 - 16 W/(m·K)

Show Material materials with Thermal conductivity of 14 - 16 W/(m·K)

Typical for Manganese Steel

Chemical properties

PropertyValue

Aluminium

0.02 %

Show Material materials with Aluminium of 0.02 %

Carbon

0.1 - 0.11 %

Show Material materials with Carbon of 0.1 - 0.11 %

Manganese

0.7 - 0.8 %

Show Material materials with Manganese of 0.7 - 0.8 %

Niobium

0.09 %

Show Material materials with Niobium of 0.09 %

Phosphorus

0.1 %

Show Material materials with Phosphorus of 0.1 %

Silicon

0.5 %

Show Material materials with Silicon of 0.5 %

Sulfur

0.025 %

Show Material materials with Sulfur of 0.025 %

Titanium

0.12 %

Show Material materials with Titanium of 0.12 %