Properties
General
| Property | Value | Temperature | Comment |
|---|---|---|---|
Density | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ at 23.0 °C | 23.0 °C | Typical for Steel |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 190 - 210 GPa Show Material materials with Elastic modulus of 190 - 210 GPa at 23.0 °C | 23.0 °C | Typical for Steel |
Elongation A50 | 14 % Show Material materials with Elongation A50 of 14 % at 23.0 °C | 23.0 °C | |
Elongation A50, transverse | 14 % Show Material materials with Elongation A50, transverse of 14 % at 23.0 °C | 23.0 °C | |
Hardness, Brinell | 283 [-] Show Material materials with Hardness, Brinell of 283 [-] at 23.0 °C | 23.0 °C | |
Hardness, Brinell, trans | 283 [-] Show Material materials with Hardness, Brinell, trans of 283 [-] at 23.0 °C | 23.0 °C | |
Hardness, Rockwell C | 30 [-] Show Material materials with Hardness, Rockwell C of 30 [-] at 23.0 °C | 23.0 °C | |
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] at 23.0 °C | 23.0 °C | Typical for Steel |
Reduction of area | 50 % Show Material materials with Reduction of area of 50 % at 23.0 °C | 23.0 °C | |
Reduction of area, transverse | 50 % Show Material materials with Reduction of area, transverse of 50 % at 23.0 °C | 23.0 °C | |
Tensile strength | 930 MPa Show Material materials with Tensile strength of 930 MPa at 23.0 °C | 23.0 °C | |
Tensile strength, transverse | 930 MPa Show Material materials with Tensile strength, transverse of 930 MPa at 23.0 °C | 23.0 °C | |
Yield strength Rp0.2 | 620 MPa Show Material materials with Yield strength Rp0.2 of 620 MPa at 23.0 °C | 23.0 °C | |
Yield strength Rp0.2, transverse | 620 MPa Show Material materials with Yield strength Rp0.2, transverse of 620 MPa at 23.0 °C | 23.0 °C |