General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 200 GPa Show Material materials with Elastic modulus of 200 GPa | |
Elongation | 23.0 °C | 11 - 21 % Show Material materials with Elongation of 11 - 21 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Steel |
Tensile strength | 23.0 °C | 910 - 1410 MPa Show Material materials with Tensile strength of 910 - 1410 MPa | |
Yield strength | 23.0 °C | 600 - 1260 MPa Show Material materials with Yield strength of 600 - 1260 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K |
Melting point | 1400 °C Show Material materials with Melting point of 1400 °C | |
Specific heat capacity | 23.0 °C | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) |
Thermal conductivity | 23.0 °C | 16 W/(m·K) Show Material materials with Thermal conductivity of 16 W/(m·K) |
Chemical properties
Property | Value |
---|---|
Carbon | 0 - 0.07 % Show Material materials with Carbon of 0 - 0.07 % |
Chromium | 15 - 17 % Show Material materials with Chromium of 15 - 17 % |
Copper | 3 - 5 % Show Material materials with Copper of 3 - 5 % |
Iron | 69.6 - 79 % Show Material materials with Iron of 69.6 - 79 % |
Manganese | 0 - 1.5 % Show Material materials with Manganese of 0 - 1.5 % |
Molybdenum | 0 - 0.6 % Show Material materials with Molybdenum of 0 - 0.6 % |
Nickel | 3 - 5 % Show Material materials with Nickel of 3 - 5 % |
Niobium | 0 - 0.45 % Show Material materials with Niobium of 0 - 0.45 % |
Phosphorus | 0 - 0.04 % Show Material materials with Phosphorus of 0 - 0.04 % |
Silicon | 0 - 1 % Show Material materials with Silicon of 0 - 1 % |
Sulfur | 0 - 0.03 % Show Material materials with Sulfur of 0 - 0.03 % |