Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 7.9 g/cm³ Show Material materials with Density of 7.9 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 210 GPa Show Material materials with Elastic modulus of 210 GPa at 23.0 °C | 23.0 °C | |
Elongation | 9.2 - 12 % Show Material materials with Elongation of 9.2 - 12 % at 23.0 °C | 23.0 °C | |
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] at 23.0 °C | 23.0 °C | Typical for Steel |
Tensile strength | 1630 - 1860 MPa Show Material materials with Tensile strength of 1630 - 1860 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 1470 - 1740 MPa Show Material materials with Yield strength of 1470 - 1740 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature |
|---|---|---|
Coefficient of thermal expansion | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K at 23.0 °C | 23.0 °C |
Specific heat capacity | 450 J/(kg·K) Show Material materials with Specific heat capacity of 450 J/(kg·K) at 23.0 °C | 23.0 °C |
Chemical properties
| Property | ||
|---|---|---|
Carbon | 0 - 0.05 % | |
Chromium | 11 - 12.5 % | |
Copper | 1.5 - 2.5 % | |
Iron | 71.5 - 79.2 % | |
Manganese | 0 - 0.5 % | |
Molybdenum | 0 - 0.5 % | |
Nickel | 7.5 - 9.5 % | |
Niobium | 0 - 0.5 % | |
Phosphorus | 0 - 0.04 % | |
Silicon | 0 - 0.5 % | |
Sulfur | 0 - 0.03 % | |
Tantalum | 0 - 0.5 % | |
Titanium | 0.8 - 1.4 % |