AISI 301L Half-Hard

Want to keep this datasheet? Save it now in your required format

Equivalent Materials

This material data has been provided by MakeItFrom.com.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Temperature
Density	7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ at 23.0 °C	23.0 °C

Mechanical

Property	Value	Temperature	Comment
Elastic modulus	220 GPa Show Material materials with Elastic modulus of 220 GPa at 23.0 °C	23.0 °C
Elongation	23 % Show Material materials with Elongation of 23 % at 23.0 °C	23.0 °C
Poisson's ratio	0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] at 23.0 °C	23.0 °C	Typical for Austenitic Stainless Steel
Shear modulus	77 GPa Show Material materials with Shear modulus of 77 GPa at 23.0 °C	23.0 °C	Typical for Austenitic Stainless Steel
Tensile strength	1070 MPa Show Material materials with Tensile strength of 1070 MPa at 23.0 °C	23.0 °C
Yield strength	790 MPa Show Material materials with Yield strength of 790 MPa at 23.0 °C	23.0 °C

Thermal

Property	Value	Temperature	Comment
Coefficient of thermal expansion	1.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-5 1/K at 23.0 °C	23.0 °C
Melting point	1230 - 1480 °C Show Material materials with Melting point of 1230 - 1480 °C		Typical for Austenitic Stainless Steel
Specific heat capacity	450 J/(kg·K) Show Material materials with Specific heat capacity of 450 J/(kg·K) at 23.0 °C	23.0 °C
Thermal conductivity	11 - 21 W/(m·K) Show Material materials with Thermal conductivity of 11 - 21 W/(m·K) at 23.0 °C	23.0 °C	Typical for Austenitic Stainless Steel

Electrical

Property	Value	Temperature	Comment
Electrical resistivity	8.5E-7 Ω·m Show Material materials with Electrical resistivity of 8.5E-7 Ω·m at 23.0 °C	23.0 °C	Typical for Austenitic Stainless Steel

Chemical properties

Property
Carbon	0 - 0.03 %
Chromium	16 - 18 %
Iron	70.7 - 78 %
Manganese	0 - 2 %
Nickel	6 - 8 %
Nitrogen	0 - 0.2 %
Phosphorus	0 - 0.05 %
Silicon	0 - 1 %
Sulfur	0 - 0.03 %

AISI 301L Half-Hard

Equivalent Materials

Ashby charts

Suggested reading

Properties